SrO*2(Al2O3) Boyko E R, Wisnyi L G Acta Crystallographica 11 (1958) 444-445 The optical properties and structures of CaO*2Al2O3 and SrO*2Al2O3 Locality: synthetic _database_code_amcsd 0009209 CELL PARAMETERS: 13.0400 9.0100 5.5500 90.000 106.502 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 625.213 Density (g/cm3): 3.267 MAX. ABS. INTENSITY / VOLUME**2: 18.22167994 RIR: 1.816 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 12.11 2.83 7.3097 1 1 0 4 14.17 27.08 6.2514 2 0 0 2 18.93 6.14 4.6885 -1 1 1 4 19.71 8.76 4.5050 0 2 0 2 22.24 15.77 3.9978 1 1 1 4 23.52 1.03 3.7826 3 1 0 4 24.35 28.40 3.6549 2 2 0 4 25.12 100.00 3.5446 -3 1 1 4 25.91 7.25 3.4383 0 2 1 4 27.21 18.95 3.2774 -2 2 1 4 28.56 3.26 3.1257 4 0 0 2 30.61 27.27 2.9203 1 3 0 4 31.92 28.17 2.8033 2 2 1 4 32.38 41.42 2.7648 3 1 1 4 32.62 2.68 2.7452 -2 0 2 2 33.69 35.87 2.6607 0 0 2 2 34.03 30.46 2.6349 -1 3 1 4 34.94 16.34 2.5681 4 2 0 4 36.48 20.24 2.4628 -5 1 1 4 36.89 8.88 2.4366 3 3 0 4 37.32 1.16 2.4095 5 1 0 4 37.66 1.12 2.3884 -4 0 2 2 37.86 4.40 2.3766 1 1 2 4 38.40 2.64 2.3443 -2 2 2 4 39.33 1.67 2.2910 0 2 2 4 40.03 1.13 2.2525 0 4 0 2 40.44 8.54 2.2305 2 0 2 2 42.51 1.39 2.1267 4 2 1 4 42.86 2.72 2.1102 -4 2 2 4 43.21 7.77 2.0937 -5 1 2 4 43.33 1.54 2.0880 3 3 1 4 43.43 13.35 2.0838 6 0 0 2 43.63 9.82 2.0743 0 4 1 4 44.47 4.73 2.0373 -2 4 1 4 44.52 12.18 2.0351 -1 3 2 4 45.37 8.44 1.9990 5 1 1 4 45.37 3.61 1.9989 2 2 2 4 46.15 6.42 1.9670 -3 3 2 4 46.52 1.50 1.9522 3 1 2 4 47.14 9.62 1.9278 -6 0 2 2 47.30 8.74 1.9217 5 3 0 4 47.70 1.23 1.9067 2 4 1 4 47.75 10.13 1.9049 1 3 2 4 50.01 13.49 1.8239 -4 4 1 4 50.91 13.79 1.7935 -3 1 3 4 50.92 1.35 1.7934 -1 1 3 4 51.22 1.67 1.7836 1 5 0 4 51.57 2.05 1.7723 -6 2 2 4 52.29 1.40 1.7496 -5 3 2 4 53.52 5.84 1.7121 -1 5 1 4 54.06 1.21 1.6964 -7 1 2 4 54.17 2.43 1.6932 5 3 1 4 55.18 1.16 1.6645 3 3 2 4 55.20 2.11 1.6639 4 2 2 4 55.27 3.03 1.6621 -5 1 3 4 55.56 5.66 1.6540 3 5 0 4 55.68 2.30 1.6507 -4 2 3 4 55.69 1.75 1.6505 0 2 3 4 55.84 5.56 1.6464 4 4 1 4 58.21 2.08 1.5849 2 4 2 4 58.27 6.21 1.5833 5 1 2 4 58.35 1.79 1.5814 -7 3 1 4 59.11 3.67 1.5629 8 0 0 2 59.11 1.28 1.5628 -3 3 3 4 59.12 8.64 1.5627 -1 3 3 4 59.28 5.37 1.5589 -6 4 1 4 59.48 4.17 1.5541 -8 0 2 2 60.29 2.52 1.5352 7 3 0 4 60.40 5.47 1.5327 -8 2 1 4 61.81 1.75 1.5009 2 2 3 4 61.98 2.21 1.4973 -7 3 2 4 62.71 3.80 1.4816 -3 5 2 4 63.40 3.03 1.4672 3 1 3 4 63.74 2.51 1.4601 2 6 0 4 64.01 1.59 1.4545 1 5 2 4 64.11 2.08 1.4525 6 0 2 2 64.47 2.90 1.4452 0 6 1 4 65.24 2.03 1.4301 -9 1 1 4 65.26 1.88 1.4296 -2 4 3 4 67.10 7.66 1.3949 6 4 1 4 67.16 1.66 1.3937 -4 4 3 4 67.40 3.13 1.3894 -9 1 2 4 67.65 1.19 1.3848 2 6 1 4 67.72 2.93 1.3837 -2 0 4 2 69.44 4.42 1.3536 4 6 0 4 70.32 1.97 1.3387 3 5 2 4 70.63 3.77 1.3336 8 2 1 4 70.67 2.12 1.3329 -7 3 3 4 70.83 2.39 1.3303 0 0 4 2 71.63 1.19 1.3174 -2 6 2 4 71.91 3.61 1.3130 -4 2 4 4 72.73 3.04 1.3002 -6 4 3 4 72.74 1.46 1.3000 2 4 3 4 73.12 1.24 1.2943 -7 5 1 4 73.79 1.52 1.2840 -3 5 3 4 73.80 1.26 1.2840 -1 5 3 4 74.51 2.80 1.2735 -9 3 2 4 74.59 1.57 1.2723 -9 1 3 4 74.62 1.08 1.2719 5 1 3 4 74.66 3.11 1.2713 -4 6 2 4 75.39 1.01 1.2609 9 3 0 4 76.13 1.19 1.2503 -6 2 4 4 76.73 1.51 1.2421 -1 3 4 4 77.13 2.17 1.2367 1 7 1 4 77.40 1.07 1.2330 1 5 3 4 79.30 2.05 1.2081 7 3 2 4 80.41 2.10 1.1942 -8 0 4 2 80.90 1.67 1.1883 2 2 4 4 81.69 2.41 1.1787 4 4 3 4 82.24 1.02 1.1722 -11 1 1 4 83.79 1.48 1.1545 -7 3 4 4 83.81 1.56 1.1542 -10 2 3 4 84.14 1.18 1.1506 4 6 2 4 84.19 1.81 1.1500 -5 7 1 4 84.45 1.10 1.1471 -7 5 3 4 84.54 1.22 1.1461 0 6 3 4 86.39 1.50 1.1263 0 8 0 2 88.12 1.68 1.1086 -9 5 2 4 88.71 1.04 1.1027 -11 1 3 4 88.97 1.58 1.1002 9 5 0 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.