Lithiophosphate Zemann J Acta Crystallographica 13 (1960) 863-867 Die kristallstruktur von lithiumphosphat, Li3PO4 Note: this is the quenchable high-temperature form _database_code_amcsd 0009246 CELL PARAMETERS: 6.1200 10.5300 4.9300 90.000 90.000 90.000 SPACE GROUP: Pmnb X-RAY WAVELENGTH: 1.541838 Cell Volume: 317.707 Density (g/cm3): 2.421 MAX. ABS. INTENSITY / VOLUME**2: 6.739649559 RIR: 0.907 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 16.84 27.88 5.2650 0 2 0 2 19.89 4.38 4.4649 0 1 1 4 22.27 100.00 3.9913 1 2 0 4 23.17 94.02 3.8393 1 0 1 4 24.68 17.97 3.6070 1 1 1 8 24.74 52.28 3.5986 0 2 1 4 28.78 15.13 3.1021 1 2 1 8 29.18 16.24 3.0600 2 0 0 2 31.28 1.49 2.8593 0 3 1 4 33.88 62.38 2.6456 2 2 0 4 34.06 33.73 2.6325 0 4 0 2 34.63 32.04 2.5905 1 3 1 8 35.57 14.53 2.5241 2 1 1 8 36.45 52.03 2.4650 0 0 2 2 37.18 1.84 2.4183 1 4 0 4 38.62 1.13 2.3312 2 2 1 8 38.78 2.06 2.3222 0 4 1 4 41.60 2.36 2.1711 1 4 1 8 43.13 4.88 2.0973 1 2 2 8 43.31 5.23 2.0892 2 3 1 8 46.91 3.95 1.9367 0 5 1 4 48.19 1.45 1.8885 2 1 2 8 49.10 4.59 1.8555 3 1 1 8 49.26 3.40 1.8498 2 4 1 8 49.36 2.79 1.8464 1 5 1 8 50.61 14.80 1.8035 2 2 2 8 50.74 7.04 1.7993 0 4 2 4 51.49 7.46 1.7747 3 2 1 8 54.38 3.31 1.6870 1 6 0 4 54.48 1.18 1.6842 2 3 2 8 55.32 6.58 1.6607 3 3 1 8 55.59 2.13 1.6534 0 6 1 4 56.21 2.03 1.6365 2 5 1 8 57.12 3.96 1.6125 3 4 0 4 57.56 1.13 1.6012 0 5 2 4 57.76 1.22 1.5961 1 6 1 8 58.12 4.87 1.5871 1 0 3 4 58.84 3.24 1.5694 1 1 3 8 58.87 3.37 1.5687 0 2 3 4 60.51 12.74 1.5300 4 0 0 2 60.85 24.49 1.5224 2 6 0 4 60.97 1.30 1.5196 1 2 3 8 62.39 1.04 1.4883 0 3 3 4 63.30 1.54 1.4692 4 2 0 4 64.43 12.87 1.4461 1 3 3 8 65.02 1.09 1.4344 3 3 2 8 65.03 5.47 1.4343 2 1 3 8 66.39 1.47 1.4080 4 2 1 8 67.25 1.38 1.3922 1 6 2 8 69.68 1.00 1.3494 3 4 2 8 70.34 4.67 1.3384 2 3 3 8 71.29 3.11 1.3228 4 4 0 4 72.75 5.67 1.2999 4 0 2 4 73.03 2.67 1.2956 0 5 3 4 73.05 11.05 1.2953 2 6 2 8 73.61 2.72 1.2868 1 8 0 4 73.77 4.86 1.2845 3 6 1 8 74.72 3.99 1.2704 3 1 3 8 74.85 1.19 1.2686 2 4 3 8 74.92 2.73 1.2675 1 5 3 8 76.62 1.20 1.2435 3 2 3 8 79.76 6.83 1.2023 3 3 3 8 80.51 1.55 1.1930 2 5 3 8 80.58 3.01 1.1922 5 2 0 4 80.93 3.48 1.1879 5 0 1 4 82.06 4.09 1.1743 2 8 1 8 82.81 1.46 1.1656 4 4 2 8 83.05 1.36 1.1629 0 3 4 4 83.90 1.21 1.1533 4 6 0 4 85.42 1.42 1.1366 2 1 4 8 86.49 1.12 1.1252 5 3 1 8 88.02 1.34 1.1096 0 7 3 4 88.38 3.69 1.1060 3 8 0 4 89.84 1.05 1.0918 1 7 3 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.