Euchroite Finney J J Acta Crystallographica 21 (1966) 437-440 Refinement of the crystal structure of euchroite, Cu2(AsO4)(OH)*3H2O _database_code_amcsd 0009302 CELL PARAMETERS: 10.0630 10.5220 6.1070 90.000 90.000 90.000 SPACE GROUP: P2_12_12_1 X-RAY WAVELENGTH: 1.541838 Cell Volume: 646.627 Density (g/cm3): 3.518 MAX. ABS. INTENSITY / VOLUME**2: 27.42637551 RIR: 2.538 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 12.17 100.00 7.2725 1 1 0 4 16.79 3.07 5.2818 0 1 1 4 16.85 26.79 5.2610 0 2 0 2 16.98 53.45 5.2208 1 0 1 4 17.63 45.22 5.0315 2 0 0 2 19.56 6.82 4.5392 2 1 0 4 22.90 1.87 3.8833 2 0 1 4 24.01 39.05 3.7058 1 2 1 4 24.43 9.30 3.6431 2 1 1 4 24.48 4.84 3.6362 2 2 0 4 26.92 6.92 3.3119 1 3 0 4 27.92 6.01 3.1959 3 1 0 4 28.57 8.16 3.1243 2 2 1 4 29.25 9.35 3.0535 0 0 2 2 30.40 21.19 2.9400 3 0 1 4 30.48 1.01 2.9325 0 1 2 4 30.60 8.42 2.9219 1 0 2 4 31.08 2.17 2.8773 2 3 0 4 31.60 52.57 2.8316 3 1 1 4 31.78 14.06 2.8154 1 1 2 4 33.95 25.92 2.6409 0 2 2 4 34.08 18.98 2.6305 0 4 0 2 34.35 13.06 2.6104 2 0 2 4 34.46 2.30 2.6028 2 3 1 4 34.96 12.52 2.5665 3 2 1 4 35.13 13.83 2.5544 1 2 2 4 35.27 13.18 2.5450 1 4 0 4 35.43 6.89 2.5336 2 1 2 4 38.32 6.12 2.3492 1 4 1 4 38.50 6.61 2.3384 2 2 2 4 38.62 7.64 2.3311 2 4 0 4 39.11 1.33 2.3030 0 3 2 4 39.68 3.05 2.2713 4 1 1 4 39.71 8.93 2.2696 4 2 0 4 40.02 8.52 2.2531 3 3 1 4 40.17 1.49 2.2450 1 3 2 4 40.87 11.63 2.2078 3 1 2 4 41.46 2.11 2.1779 2 4 1 4 42.49 3.68 2.1274 4 2 1 4 43.20 3.30 2.0941 2 3 2 4 43.62 4.35 2.0750 3 2 2 4 43.73 1.65 2.0699 3 4 0 4 43.96 8.25 2.0598 1 5 0 4 44.31 4.63 2.0442 4 3 0 4 45.46 1.02 1.9953 1 0 3 4 46.31 7.10 1.9604 3 4 1 4 46.32 2.72 1.9603 1 1 3 4 46.45 5.86 1.9550 1 4 2 4 46.53 1.39 1.9518 1 5 1 4 46.79 11.01 1.9416 4 0 2 4 46.87 1.00 1.9385 4 3 1 4 47.63 5.34 1.9094 4 1 2 4 47.91 7.33 1.8986 3 3 2 4 48.22 3.59 1.8871 2 0 3 4 48.82 1.21 1.8656 1 2 3 4 49.04 6.46 1.8574 2 1 3 4 49.17 1.79 1.8529 2 4 2 4 49.25 1.63 1.8502 2 5 1 4 51.25 2.34 1.7826 3 5 0 4 51.44 4.41 1.7763 2 2 3 4 52.42 4.34 1.7456 5 3 0 4 52.52 1.86 1.7425 4 4 1 4 53.36 3.79 1.7169 3 1 3 4 53.55 7.23 1.7112 3 5 1 4 53.67 2.67 1.7076 1 5 2 4 53.98 2.16 1.6987 4 3 2 4 54.73 1.46 1.6772 6 0 0 2 55.26 3.84 1.6624 1 6 1 4 55.37 7.00 1.6594 5 1 2 4 55.48 4.88 1.6563 6 1 0 4 57.06 3.15 1.6141 4 5 0 4 57.68 1.20 1.5983 2 6 1 4 59.03 1.91 1.5649 4 1 3 4 59.14 4.95 1.5622 4 4 2 4 59.28 1.82 1.5589 3 3 3 4 59.83 1.02 1.5459 6 2 1 4 60.10 2.92 1.5395 3 5 2 4 60.37 3.12 1.5333 2 4 3 4 60.65 1.35 1.5267 0 0 4 2 60.92 6.97 1.5207 0 6 2 4 61.15 5.73 1.5155 5 3 2 4 61.26 4.41 1.5131 6 3 0 4 61.36 1.53 1.5109 0 1 4 4 61.42 4.90 1.5095 1 0 4 4 61.58 3.05 1.5061 3 6 1 4 61.69 7.32 1.5036 1 6 2 4 62.12 3.42 1.4942 1 1 4 4 63.95 5.28 1.4559 6 1 2 4 63.96 3.43 1.4557 2 6 2 4 64.38 2.31 1.4471 2 1 4 4 64.61 1.05 1.4425 4 3 3 4 64.81 2.23 1.4386 4 6 0 4 65.97 1.82 1.4161 5 4 2 4 65.98 3.81 1.4158 6 2 2 4 66.07 1.09 1.4142 6 4 0 4 66.41 1.53 1.4077 2 2 4 4 66.56 2.60 1.4049 2 5 3 4 66.73 2.40 1.4018 2 7 1 4 67.53 4.44 1.3871 7 1 1 4 67.56 1.04 1.3865 1 3 4 4 67.87 1.01 1.3810 5 2 3 4 68.06 1.10 1.3776 3 1 4 4 68.39 2.06 1.3717 3 7 0 4 69.29 1.11 1.3560 4 4 3 4 69.31 3.10 1.3558 6 3 2 4 69.73 2.77 1.3486 2 3 4 4 70.34 2.31 1.3384 3 7 1 4 70.45 2.61 1.3366 1 7 2 4 71.64 1.10 1.3172 1 6 3 4 71.90 2.36 1.3131 5 5 2 4 72.00 1.25 1.3116 6 5 0 4 72.15 4.14 1.3092 1 4 4 4 72.57 1.75 1.3026 2 7 2 4 72.76 2.55 1.2997 7 3 1 4 73.37 1.95 1.2904 4 7 0 4 73.76 1.22 1.2846 2 6 3 4 74.38 1.12 1.2754 1 8 1 4 74.58 1.09 1.2725 2 8 0 4 74.97 1.71 1.2668 4 2 4 4 75.11 1.15 1.2648 4 5 3 4 77.23 1.05 1.2353 3 6 3 4 78.42 2.45 1.2195 7 3 2 4 79.29 2.27 1.2083 5 1 4 4 79.59 1.72 1.2045 1 1 5 4 82.84 1.44 1.1652 7 5 1 4 83.49 1.11 1.1578 2 2 5 4 84.26 2.43 1.1492 5 3 4 4 86.75 1.40 1.1225 2 6 4 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.