Cliffordite Galy J, Meunier G Acta Crystallographica B27 (1971) 608-616 A propos de la cliffordite UTe3O8. Le Systeme UO3-TeO2 a 700 C. Structure cristalline de UTe3O9 Locality: synthetic Sample: T = 700 C _database_code_amcsd 0009388 CELL PARAMETERS: 11.3700 11.3700 11.3700 90.000 90.000 90.000 SPACE GROUP: Pa3 X-RAY WAVELENGTH: 1.541838 Cell Volume: 1469.878 Density (g/cm3): 6.911 MAX. ABS. INTENSITY / VOLUME**2: 231.1050802 RIR: 10.888 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 15.59 11.00 5.6850 2 0 0 6 17.44 3.03 5.0848 2 1 0 12 19.12 13.34 4.6418 2 1 1 24 22.11 24.78 4.0199 2 2 0 12 23.47 8.72 3.7900 2 2 1 24 27.17 100.00 3.2822 2 2 2 8 28.30 6.44 3.1535 3 0 2 12 29.39 5.16 3.0388 3 2 1 24 29.39 1.72 3.0388 3 1 2 24 31.47 33.51 2.8425 4 0 0 6 32.47 10.95 2.7576 4 1 0 12 32.47 11.35 2.7576 3 2 2 24 33.44 6.01 2.6799 4 1 1 24 35.30 10.64 2.5424 4 0 2 12 35.30 4.36 2.5424 4 2 0 12 36.20 4.20 2.4811 4 1 2 24 38.80 8.58 2.3209 4 2 2 24 39.63 1.50 2.2740 4 3 0 12 40.45 2.77 2.2298 4 3 1 24 42.83 2.62 2.1114 4 2 3 24 45.11 30.82 2.0100 4 4 0 12 45.85 3.81 1.9793 4 4 1 24 46.58 2.85 1.9499 4 3 3 24 48.01 13.28 1.8950 4 4 2 24 49.41 3.16 1.8445 6 1 1 24 50.79 5.00 1.7978 6 0 2 12 50.79 12.58 1.7978 6 2 0 12 51.46 4.74 1.7757 5 0 4 12 51.46 3.71 1.7757 6 1 2 24 52.13 1.45 1.7544 5 4 1 24 53.46 19.30 1.7141 6 2 2 24 54.11 5.02 1.6949 5 2 4 24 54.11 2.44 1.6949 6 3 0 12 54.76 2.26 1.6764 6 1 3 24 56.04 4.45 1.6411 4 4 4 8 56.67 9.91 1.6243 6 3 2 24 57.30 1.25 1.6080 5 4 3 24 58.54 2.12 1.5767 6 0 4 12 58.54 1.49 1.5767 6 4 0 12 60.98 5.28 1.5194 6 4 2 24 60.98 8.30 1.5194 6 2 4 24 61.58 2.81 1.5060 5 4 4 24 61.58 1.23 1.5060 7 2 2 24 63.95 2.39 1.4558 6 3 4 24 64.54 1.07 1.4440 6 1 5 24 65.70 1.17 1.4212 8 0 0 6 66.27 1.50 1.4103 8 1 0 12 66.85 1.35 1.3996 7 4 1 24 67.99 7.21 1.3788 8 0 2 12 67.99 2.21 1.3788 6 4 4 24 67.99 2.16 1.3788 8 2 0 12 70.25 3.28 1.3400 6 6 0 12 71.36 1.34 1.3217 8 3 1 24 71.36 1.85 1.3217 8 1 3 24 72.47 3.09 1.3042 6 6 2 24 74.67 1.40 1.2712 8 4 0 12 74.67 1.25 1.2712 8 0 4 12 76.84 8.21 1.2406 8 4 2 24 76.84 3.43 1.2406 8 2 4 24 77.38 1.34 1.2332 7 0 6 12 79.00 4.21 1.2120 6 6 4 24 79.53 1.40 1.2052 8 5 0 12 79.53 1.97 1.2052 7 2 6 24 81.67 1.13 1.1790 8 5 2 24 82.20 1.03 1.1727 7 3 6 24 83.26 1.90 1.1604 8 4 4 24 84.32 1.46 1.1485 9 1 4 24 85.38 1.81 1.1370 8 6 0 12 85.38 1.63 1.1370 8 0 6 12 85.91 1.08 1.1314 7 4 6 24 87.49 2.66 1.1149 8 2 6 24 87.49 5.12 1.1149 10 2 0 12 88.02 1.29 1.1096 8 5 4 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.