Sidwillite Krebs B Acta Crystallographica B28 (1972) 2222-2231 Die kristallstruktur von MoO3*2H2O Locality: synthetic _database_code_amcsd 0009439 10.476 13.822 10.606 90 91.62 90 P2_1/n atom x y z Biso B(1,1) B(2,2) B(3,3) B(1,2) B(1,3) B(2,3) Mo1 .11729 .24968 .14710 .99 .00219 .00153 .00193 -.00002 -.00002 -.00001 Mo2 .39389 .25528 .35964 .98 .00201 .00151 .00204 -.00006 -.00010 .00005 Mo3 -.13721 .25189 .39802 1.04 .00229 .00156 .00206 -.00002 -.00017 .00008 Mo4 .15387 .24499 .61827 1.01 .00209 .00160 .00206 -.00005 -.00015 .00004 O1 .0216 .2543 -.0255 1.20 .00228 .00221 .00174 .00024 -.00024 -.00034 O2 .2313 .2085 .2661 1.14 .00175 .00217 .00184 .00001 -.00041 -.00018 O3 .2635 .2087 .0192 1.21 .00184 .00225 .00214 .00003 -.00068 -.00008 O4 -.0266 .2438 .2287 1.39 .00232 .00291 .00204 .00004 -.00049 -.00008 O5 .4812 .2623 .2190 1.46 .00224 .00319 .00182 -.00048 -.00058 .00027 O6 .2716 .2094 .5116 1.15 .00195 .00205 .00214 .00053 -.00019 .00017 O7 -.2695 .2958 .2652 1.20 .00171 .00237 .00202 .00018 -.00041 -.00001 O8 .0146 .2539 .4779 1.50 .00269 .00302 .00194 .00021 -.00003 .00003 O9 .1520 .3685 .1431 1.65 .00327 .00212 .00422 -.00015 -.00068 .00006 O10 .3423 .3727 .3770 1.60 .00338 .00209 .00390 -.00016 .00043 -.00016 O11 -.1723 .1334 .3897 1.78 .00438 .00238 .00417 -.00010 -.00014 -.00005 O12 .1737 .3662 .6288 1.86 .00448 .00236 .00404 -.00048 -.00014 -.00037 O13 .0838 .0889 .1107 1.47 .00303 .00184 .00391 -.0005 .00023 -.00019 O14 .4146 .0910 .3514 1.59 .00365 .00146 .00486 .00049 .00006 -.00025 O15 -.0884 .4106 .3610 1.40 .00296 .00175 .00343 -.00059 .00029 .00011 O16 .0920 .0857 .6003 1.35 .00299 .00154 .00369 -.00029 -.00052 -.00049 O17 .3593 .5011 .1288 2.07 .00429 .00275 .00539 -.00027 .0003 -.00047 O18 .3612 .5119 .6243 2.52 .00391 .00400 .00608 .00014 .00117 -.00059 O19 .1426 .5035 .3762 1.89 .00362 .00259 .00503 .00020 -.00060 -.00054 O20 -.1339 .4896 .1234 2.07 .00320 .00279 .00599 .00009 -.00001 -.00021 H1 .053 .047 .129 4 H2 .097 .082 .037 4 H3 .389 .061 .267 4 H4 .476 .063 .369 4 H5 -.02 .427 .384 4 H6 -.11 .432 .279 4 H7 .103 .061 .53 4 H8 .007 .067 .631 4 H9 .28 .464 .134 4 H10 .339 .528 .197 4 H11 .353 .547 .697 4 H12 .308 .449 .63 4 H13 .223 .473 .356 4 H14 .126 .508 .45 4 H15 -.138 .455 .052 4 H16 -.185 .555 .122 4