SrFCl Sauvage M Acta Crystallographica B30 (1974) 2786-2787 Refinement of the structures of SrFCl and BaFCl Locality: synthetic Note: matlockite structure _database_code_amcsd 0009522 CELL PARAMETERS: 4.1259 4.1259 6.9579 90.000 90.000 90.000 SPACE GROUP: P4/nmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 118.445 Density (g/cm3): 3.983 MAX. ABS. INTENSITY / VOLUME**2: 39.74846378 RIR: 3.249 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 12.72 20.07 6.9579 0 0 1 2 25.09 89.91 3.5489 1 0 1 8 25.61 25.57 3.4790 0 0 2 2 30.64 96.90 2.9175 1 1 0 4 33.30 3.57 2.6905 1 1 1 8 33.70 100.00 2.6597 1 0 2 8 40.35 80.36 2.2354 1 1 2 8 43.89 62.65 2.0629 2 0 0 4 44.83 27.75 2.0218 1 0 3 8 45.88 3.17 1.9778 2 0 1 8 50.25 13.84 1.8155 1 1 3 8 51.22 26.44 1.7835 2 1 1 16 51.50 14.62 1.7744 2 0 2 8 56.45 37.90 1.6301 2 1 2 16 57.50 24.80 1.6028 1 0 4 8 60.02 1.35 1.5414 2 0 3 8 63.81 17.33 1.4587 2 2 0 4 64.54 16.46 1.4439 2 1 3 16 67.28 4.80 1.3916 0 0 5 2 69.69 4.87 1.3492 3 0 1 8 69.93 5.66 1.3453 2 2 2 8 71.56 1.59 1.3186 1 0 5 8 72.44 13.58 1.3047 3 1 0 8 74.14 7.61 1.2790 3 0 2 8 75.05 20.58 1.2657 2 1 4 16 75.73 6.93 1.2560 1 1 5 8 78.26 17.12 1.2216 3 1 2 16 81.34 3.98 1.1830 3 0 3 8 83.86 9.54 1.1536 2 0 5 8 85.37 4.61 1.1371 3 1 3 16 86.12 5.25 1.1291 3 2 1 16 87.35 2.64 1.1164 1 0 6 8 87.88 1.79 1.1110 2 1 5 16 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.