Cervantite Thornton G Acta Crystallographica B33 (1977) 1271-1273 A neutron diffraction study of a-Sb2O4 Locality: synthetic _database_code_amcsd 0009585 CELL PARAMETERS: 5.4560 4.8140 11.7870 90.000 90.000 90.000 SPACE GROUP: Pna2_1 X-RAY WAVELENGTH: 1.541838 Cell Volume: 309.588 Density (g/cm3): 6.597 MAX. ABS. INTENSITY / VOLUME**2: 182.2572394 RIR: 8.996 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 19.92 6.46 4.4566 0 1 1 2 24.66 1.63 3.6098 1 1 0 4 25.81 36.67 3.4515 1 1 1 4 29.01 100.00 3.0782 1 1 2 4 29.34 3.58 3.0439 0 1 3 2 30.33 29.80 2.9467 0 0 4 1 32.83 3.37 2.7280 2 0 0 2 33.72 11.83 2.6582 1 1 3 4 33.72 13.33 2.6577 2 0 1 2 36.29 10.51 2.4756 2 0 2 2 37.36 11.64 2.4070 0 2 0 2 39.48 2.52 2.2827 1 1 4 4 40.25 4.47 2.2408 2 0 3 2 40.99 1.78 2.2016 2 1 2 4 41.72 1.63 2.1648 1 2 1 4 43.89 1.58 2.0629 1 2 2 4 45.30 4.95 2.0019 2 0 4 2 45.98 6.57 1.9738 1 1 5 4 47.32 2.45 1.9210 1 2 3 4 48.86 17.76 1.8641 0 2 4 2 50.57 2.52 1.8049 2 2 0 4 51.20 10.82 1.7841 2 2 1 4 51.22 6.15 1.7837 2 0 5 2 53.07 6.94 1.7258 2 2 2 4 53.07 20.42 1.7255 1 1 6 4 53.89 10.81 1.7013 3 1 0 4 54.49 4.40 1.6839 3 1 1 4 56.07 8.47 1.6401 2 2 3 4 57.25 1.47 1.6093 1 2 5 4 57.84 3.57 1.5942 2 0 6 2 58.01 1.55 1.5900 0 3 1 2 59.18 3.67 1.5612 3 1 3 4 60.12 2.30 1.5391 2 2 4 4 60.67 2.02 1.5265 1 3 1 4 60.69 3.87 1.5260 1 1 7 4 62.34 9.69 1.4895 1 3 2 4 63.10 3.44 1.4734 0 0 8 1 63.10 10.41 1.4734 3 1 4 4 64.73 1.02 1.4402 3 2 1 4 65.07 3.52 1.4334 1 3 3 4 65.09 4.37 1.4331 2 2 5 4 65.10 3.09 1.4329 2 0 7 2 67.95 1.94 1.3796 3 1 5 4 68.28 1.18 1.3737 2 3 1 4 69.36 1.16 1.3550 4 0 1 2 70.91 2.54 1.3291 2 2 6 4 70.92 4.55 1.3289 4 0 2 2 71.06 1.14 1.3265 0 3 5 2 72.44 1.01 1.3046 2 3 3 4 73.47 1.19 1.2890 1 3 5 4 75.68 5.28 1.2566 0 2 8 2 77.53 1.47 1.2312 2 2 7 4 77.54 1.01 1.2311 1 1 9 4 79.02 3.94 1.2117 1 3 6 4 79.67 1.36 1.2035 0 4 0 2 79.69 1.61 1.2033 3 3 0 4 80.20 1.72 1.1968 3 1 7 4 81.53 1.56 1.1807 2 0 9 2 82.48 1.71 1.1694 1 4 1 4 83.01 4.83 1.1634 4 2 2 4 84.14 1.18 1.1505 3 3 3 4 84.98 1.02 1.1414 2 2 8 4 85.47 1.34 1.1360 4 2 3 4 86.42 1.32 1.1260 1 4 3 4 86.95 4.57 1.1205 1 1 10 4 86.95 2.64 1.1204 4 0 6 2 87.57 2.35 1.1142 0 4 4 2 87.59 4.32 1.1140 3 3 4 4 87.60 4.58 1.1138 3 1 8 4 89.37 1.31 1.0963 2 4 1 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.