Willemite Klaska K-H, Eck J C, Pohl D Acta Crystallographica B34 (1978) 3324-3325 New investigation of willemite Locality: Synthetic Note: Anisotropic displacement parameters are from ICSD _database_code_amcsd 0009645 CELL PARAMETERS: 13.9480 13.9480 9.3150 90.000 90.000 120.000 SPACE GROUP: R-3 X-RAY WAVELENGTH: 1.541838 Cell Volume: 1569.413 Density (g/cm3): 4.245 MAX. ABS. INTENSITY / VOLUME**2: 38.26235990 RIR: 2.935 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 12.69 22.04 6.9740 1 1 0 6 17.50 1.44 5.0677 0 2 1 6 20.44 4.25 4.3457 0 1 2 6 21.68 3.59 4.0996 2 1 1 6 21.68 9.30 4.0996 3 -1 1 6 22.08 28.31 4.0264 3 0 0 6 25.55 73.55 3.4870 2 2 0 6 27.35 1.89 3.2604 -1 3 2 6 27.35 2.45 3.2604 1 2 2 6 28.31 3.02 3.1525 1 3 1 6 28.31 2.05 3.1525 -1 4 1 6 31.54 43.39 2.8366 2 -1 3 6 31.54 44.46 2.8366 1 1 3 6 34.01 2.39 2.6359 1 4 0 6 34.01 97.61 2.6359 4 1 0 6 35.43 1.86 2.5338 0 4 2 6 38.84 28.31 2.3189 2 2 3 6 38.84 25.85 2.3189 4 -2 3 6 39.41 2.61 2.2866 1 0 4 6 40.69 2.05 2.2172 2 4 1 6 42.14 5.53 2.1445 5 0 2 6 43.63 1.86 2.0745 3 -1 4 6 44.18 1.88 2.0498 6 -2 2 6 45.03 8.68 2.0132 6 0 0 6 45.12 1.21 2.0095 -1 5 3 6 46.16 2.90 1.9666 -1 6 2 6 46.77 1.54 1.9422 7 -3 1 6 46.98 10.16 1.9342 2 5 0 6 48.95 23.05 1.8609 6 -3 3 6 48.95 20.87 1.8609 3 3 3 6 49.92 1.76 1.8267 3 4 2 6 50.51 1.63 1.8071 1 6 1 6 53.09 2.46 1.7249 1 2 5 6 54.31 3.46 1.6892 0 6 3 6 54.31 4.22 1.6892 6 0 3 6 54.75 1.80 1.6766 0 5 4 6 55.76 1.35 1.6487 8 -2 1 6 55.76 1.64 1.6487 6 2 1 6 56.01 2.65 1.6417 7 -2 3 6 56.01 2.28 1.6417 2 5 3 6 56.01 1.75 1.6417 -2 7 3 6 56.01 1.81 1.6417 5 2 3 6 56.52 1.35 1.6282 4 -1 5 6 57.61 8.76 1.5999 1 7 0 6 57.61 5.22 1.5999 7 1 0 6 58.11 1.75 1.5874 5 1 4 6 59.55 13.37 1.5525 0 0 6 2 60.87 4.82 1.5219 3 6 0 6 60.87 4.09 1.5219 6 3 0 6 60.94 1.16 1.5202 8 -4 3 6 60.94 1.09 1.5202 4 4 3 6 64.31 1.08 1.4486 3 0 6 6 65.65 1.92 1.4222 -1 8 3 6 65.65 18.30 1.4222 1 7 3 6 65.65 17.19 1.4222 8 -1 3 6 65.65 2.10 1.4222 7 1 3 6 65.85 4.18 1.4183 4 -2 6 6 65.85 3.13 1.4183 2 2 6 6 67.11 6.52 1.3948 5 5 0 6 68.69 10.23 1.3665 6 3 3 6 68.69 9.92 1.3665 -3 9 3 6 70.11 4.73 1.3421 9 0 0 6 70.38 9.28 1.3377 4 1 6 6 70.38 9.18 1.3377 -1 5 6 6 75.97 1.76 1.2526 7 4 0 6 77.67 1.56 1.2294 0 6 6 6 77.67 1.57 1.2294 6 0 6 6 78.91 1.52 1.2132 10 -2 3 6 78.91 1.35 1.2132 2 8 3 6 79.10 1.72 1.2107 2 5 6 6 79.10 1.42 1.2107 7 -2 6 6 83.16 3.31 1.1616 -4 11 3 6 83.16 3.01 1.1616 7 4 3 6 84.51 4.01 1.1465 10 1 0 6 87.56 1.81 1.1142 1 7 6 6 87.56 2.55 1.1142 8 -1 6 6 87.56 1.09 1.1142 7 1 6 6 87.56 1.24 1.1142 -1 8 6 6 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.