In0.21 O3 W Labbe P, Goreaud M, Raveau B, Monier J Acta Crystallographica B35 (1979) 1557-1564 Etude comparative des structures Mx W O3 de type bronze hexagonal. II. Evolution structurale dans la serie des bronzes Inx W O3 (x equals a number between 0.12 and 0.33) _cod_database_code 1001042 _database_code_amcsd 0009678 CELL PARAMETERS: 7.3883 7.3883 7.5065 90.000 90.000 120.000 SPACE GROUP: P6_3/mcm X-RAY WAVELENGTH: 1.541838 Cell Volume: 354.860 Density (g/cm3): 7.205 MAX. ABS. INTENSITY / VOLUME**2: 278.6564688 RIR: 12.594 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.84 26.10 6.3985 1 0 0 6 23.71 38.66 3.7532 0 0 2 2 24.09 8.02 3.6941 1 1 0 6 26.90 5.74 3.3145 1 1 1 12 27.55 30.00 3.2374 1 0 2 12 27.89 100.00 3.1992 2 0 0 6 34.05 17.17 2.6328 1 1 2 12 36.92 39.43 2.4347 2 0 2 12 37.18 1.01 2.4184 2 1 0 12 39.13 4.09 2.3019 2 1 1 24 42.38 1.72 2.1328 3 0 0 6 43.69 1.52 2.0717 1 1 3 12 44.57 7.19 2.0329 2 1 2 24 48.51 8.68 1.8766 0 0 4 2 49.13 5.53 1.8543 3 0 2 12 49.34 20.59 1.8471 2 2 0 6 50.69 3.21 1.8008 1 0 4 12 51.50 2.86 1.7746 3 1 0 12 52.63 1.66 1.7389 2 1 3 24 53.02 6.52 1.7270 3 1 1 24 54.87 2.70 1.6731 1 1 4 12 55.44 14.60 1.6573 2 2 2 12 56.88 21.05 1.6187 2 0 4 12 57.44 7.65 1.6043 3 1 2 24 57.62 11.51 1.5996 4 0 0 6 62.66 1.76 1.4826 2 1 4 24 63.19 9.21 1.4715 4 0 2 12 64.36 3.43 1.4475 3 1 3 24 66.35 1.27 1.4089 3 0 4 12 68.33 2.52 1.3727 4 1 1 24 68.65 2.47 1.3671 3 2 2 24 71.69 9.63 1.3164 2 2 4 12 72.19 2.16 1.3086 4 1 2 24 73.44 2.68 1.2894 3 1 4 24 76.08 1.34 1.2511 0 0 6 2 78.44 1.63 1.2193 4 1 3 24 78.58 6.68 1.2174 4 0 4 12 79.22 1.95 1.2092 4 2 0 12 82.85 4.88 1.1652 2 0 6 12 84.11 1.96 1.1509 4 2 2 24 84.54 1.44 1.1462 3 1 5 24 86.97 1.06 1.1202 4 1 4 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.