In0.24 O3 W Labbe P, Goreaud M, Raveau B, Monier J Acta Crystallographica B35 (1979) 1557-1564 Etude comparative des structures Mx W O3 de type bronze hexagonal. II. Evolution structurale dans la serie des bronzes Inx W O3 (x equals a number between 0.12 and 0.33) _cod_database_code 1001043 _database_code_amcsd 0009679 CELL PARAMETERS: 7.3837 7.3837 7.5012 90.000 90.000 120.000 SPACE GROUP: P6_3/mcm X-RAY WAVELENGTH: 1.541838 Cell Volume: 354.168 Density (g/cm3): 7.322 MAX. ABS. INTENSITY / VOLUME**2: 285.0201924 RIR: 12.675 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.85 21.02 6.3945 1 0 0 6 23.72 35.85 3.7506 0 0 2 2 24.11 7.27 3.6918 1 1 0 6 26.92 5.23 3.3124 1 1 1 12 27.57 32.57 3.2352 1 0 2 12 27.91 100.00 3.1972 2 0 0 6 34.08 18.89 2.6311 1 1 2 12 36.94 36.75 2.4331 2 0 2 12 39.16 3.77 2.3004 2 1 1 24 42.41 1.55 2.1315 3 0 0 6 43.72 1.42 2.0703 1 1 3 12 44.60 8.00 2.0316 2 1 2 24 48.55 8.96 1.8753 0 0 4 2 49.17 5.91 1.8531 3 0 2 12 49.37 20.66 1.8459 2 2 0 6 50.73 2.51 1.7995 1 0 4 12 51.53 2.69 1.7735 3 1 0 12 52.67 1.56 1.7378 2 1 3 24 53.06 6.09 1.7259 3 1 1 24 54.91 2.27 1.6720 1 1 4 12 55.48 14.65 1.6562 2 2 2 12 56.93 21.66 1.6176 2 0 4 12 57.48 7.60 1.6033 3 1 2 24 57.66 10.99 1.5986 4 0 0 6 62.71 1.41 1.4816 2 1 4 24 63.23 8.89 1.4706 4 0 2 12 64.41 3.25 1.4466 3 1 3 24 66.40 1.07 1.4079 3 0 4 12 68.38 2.34 1.3719 4 1 1 24 68.70 2.66 1.3662 3 2 2 24 71.75 9.89 1.3155 2 2 4 12 72.24 2.19 1.3078 4 1 2 24 73.49 2.38 1.2885 3 1 4 24 76.14 1.24 1.2502 0 0 6 2 78.50 1.53 1.2185 4 1 3 24 78.64 6.60 1.2166 4 0 4 12 79.28 1.88 1.2084 4 2 0 12 82.92 4.58 1.1644 2 0 6 12 84.17 2.03 1.1502 4 2 2 24 84.61 1.33 1.1454 3 1 5 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.