In0.28 O3 W Labbe P, Goreaud M, Raveau B, Monier J Acta Crystallographica B35 (1979) 1557-1564 Etude comparative des structures Mx W O3 de type bronze hexagonal. II. Evolution structurale dans la serie des bronzes Inx W O3 (x equals a number between 0.12 and 0.33) _cod_database_code 1001044 _database_code_amcsd 0009680 CELL PARAMETERS: 7.3673 7.3673 7.5020 90.000 90.000 120.000 SPACE GROUP: P6_3/mcm X-RAY WAVELENGTH: 1.541838 Cell Volume: 352.634 Density (g/cm3): 7.462 MAX. ABS. INTENSITY / VOLUME**2: 297.1661507 RIR: 12.967 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.88 17.50 6.3803 1 0 0 6 23.72 33.71 3.7510 0 0 2 2 24.16 5.83 3.6837 1 1 0 6 26.97 4.12 3.3065 1 1 1 12 27.59 33.19 3.2336 1 0 2 12 27.97 100.00 3.1901 2 0 0 6 34.11 18.28 2.6282 1 1 2 12 36.99 35.69 2.4301 2 0 2 12 39.24 2.91 2.2958 2 1 1 24 42.51 1.56 2.1268 3 0 0 6 43.75 1.10 2.0690 1 1 3 12 44.67 7.93 2.0285 2 1 2 24 48.54 8.48 1.8755 0 0 4 2 49.25 5.91 1.8501 3 0 2 12 49.49 20.30 1.8418 2 2 0 6 50.74 2.59 1.7994 1 0 4 12 51.65 2.50 1.7696 3 1 0 12 52.73 1.19 1.7359 2 1 3 24 53.18 4.55 1.7223 3 1 1 24 54.94 2.27 1.6713 1 1 4 12 55.59 14.47 1.6533 2 2 2 12 56.96 20.84 1.6168 2 0 4 12 57.59 7.06 1.6004 3 1 2 24 57.80 11.19 1.5951 4 0 0 6 62.76 1.67 1.4805 2 1 4 24 63.36 9.30 1.4679 4 0 2 12 64.51 2.43 1.4445 3 1 3 24 66.47 1.23 1.4067 3 0 4 12 68.55 1.84 1.3689 4 1 1 24 68.85 2.60 1.3636 3 2 2 24 71.84 9.31 1.3141 2 2 4 12 72.40 2.02 1.3053 4 1 2 24 73.59 2.51 1.2871 3 1 4 24 76.13 1.17 1.2503 0 0 6 2 78.65 1.20 1.2165 4 1 3 24 78.76 6.39 1.2151 4 0 4 12 79.49 1.93 1.2058 4 2 0 12 82.94 4.59 1.1641 2 0 6 12 83.84 1.10 1.1539 3 2 4 24 84.38 2.21 1.1479 4 2 2 24 84.70 1.01 1.1444 3 1 5 24 87.20 1.16 1.1179 4 1 4 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.