Heazlewoodite Parise J B Acta Crystallographica B36 (1980) 1179-1180 Structure of hazelwoodite (Ni3S2) Locality: synthetic _database_code_amcsd 0009709 CELL PARAMETERS: 4.0718 4.0718 4.0718 89.459 89.459 89.459 SPACE GROUP: R32 X-RAY WAVELENGTH: 1.541838 Cell Volume: 67.500 Density (g/cm3): 5.908 MAX. ABS. INTENSITY / VOLUME**2: 70.07607463 RIR: 3.862 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 21.83 54.47 4.0714 1 0 0 6 31.21 100.00 2.8656 0 -1 1 3 37.92 39.00 2.3729 1 1 1 2 38.41 12.39 2.3434 1 -1 1 6 44.51 31.38 2.0357 2 0 0 6 49.90 60.40 1.8277 2 1 0 6 50.30 49.21 1.8140 0 -1 2 6 54.80 14.39 1.6753 2 1 1 6 55.36 56.40 1.6596 2 -1 1 6 55.55 17.68 1.6544 1 -2 1 6 68.57 1.76 1.3686 2 2 1 6 69.23 2.26 1.3571 2 -1 2 6 69.23 2.26 1.3571 3 0 0 6 69.56 3.86 1.3515 2 -2 1 6 73.32 10.28 1.2911 3 1 0 6 77.88 2.57 1.2265 3 -1 1 6 78.20 9.86 1.2224 -1 -1 3 6 81.05 1.27 1.1865 2 2 2 2 82.29 3.55 1.1717 2 -2 2 6 85.65 7.31 1.1341 3 2 0 6 86.57 8.36 1.1244 0 -2 3 6 89.38 12.55 1.0962 3 2 1 6 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.