Rooseveltite Bedlivy D, Mereiter K Acta Crystallographica B38 (1982) 1559-1561 Structure of alpha-BiAsO4 (rooseveltite) Locality: synthetic Note: AnisoU's from ICSD _database_code_amcsd 0009764 CELL PARAMETERS: 6.8790 7.1590 6.7320 90.000 104.840 90.000 SPACE GROUP: P2_1/n X-RAY WAVELENGTH: 1.541838 Cell Volume: 320.471 Density (g/cm3): 7.210 MAX. ABS. INTENSITY / VOLUME**2: 163.7584923 RIR: 7.396 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 16.44 2.55 5.3922 -1 0 1 2 18.21 7.88 4.8721 1 1 0 4 18.42 30.98 4.8154 0 1 1 4 20.62 17.03 4.3071 -1 1 1 4 21.41 4.79 4.1498 1 0 1 2 24.80 8.52 3.5903 1 1 1 4 24.87 3.06 3.5795 0 2 0 2 26.81 50.63 3.3248 2 0 0 2 27.41 10.43 3.2537 0 0 2 2 28.32 100.00 3.1518 1 2 0 4 28.46 1.83 3.1363 0 2 1 4 29.62 7.02 3.0163 -2 1 1 4 29.62 12.33 3.0154 2 1 0 4 30.03 22.27 2.9760 -1 1 2 4 30.17 48.25 2.9621 0 1 2 4 33.05 1.07 2.7105 1 2 1 4 33.23 24.14 2.6961 -2 0 2 2 35.58 11.60 2.5231 -2 1 2 4 35.60 1.74 2.5216 2 1 1 4 35.95 15.84 2.4980 1 1 2 4 37.23 11.60 2.4151 -1 2 2 4 40.25 7.14 2.2404 0 3 1 4 40.30 8.79 2.2381 -1 0 3 2 41.38 3.61 2.1822 -1 3 1 4 41.50 6.20 2.1762 -3 1 1 4 41.97 7.91 2.1527 2 2 1 4 42.27 1.45 2.1379 1 2 2 4 42.70 4.15 2.1174 3 1 0 4 43.76 4.72 2.0687 1 3 1 4 45.01 1.89 2.0142 -3 1 2 4 45.49 1.24 1.9941 -2 1 3 4 45.52 21.78 1.9929 2 1 2 4 46.55 2.50 1.9512 3 0 1 2 46.86 3.95 1.9389 -2 3 1 4 46.86 1.68 1.9387 2 3 0 4 47.14 15.35 1.9281 -1 3 2 4 47.23 3.09 1.9243 0 3 2 4 47.29 3.18 1.9222 1 0 3 2 48.30 13.85 1.8845 3 2 0 4 48.35 1.42 1.8825 3 1 1 4 49.11 7.34 1.8551 0 2 3 4 50.40 20.38 1.8107 -3 2 2 4 50.80 1.49 1.7974 -3 0 3 2 50.84 3.50 1.7960 -2 2 3 4 51.03 8.25 1.7897 0 4 0 2 51.12 2.36 1.7869 -2 3 2 4 51.13 1.74 1.7864 2 3 1 4 51.39 15.04 1.7779 1 3 2 4 52.98 2.60 1.7282 1 4 0 4 54.91 1.65 1.6722 -4 1 1 4 55.24 8.17 1.6629 -4 0 2 2 55.26 2.92 1.6624 4 0 0 2 55.70 2.78 1.6501 -3 3 1 4 55.95 1.50 1.6434 1 4 1 4 56.14 4.40 1.6382 -1 1 4 4 56.57 2.70 1.6269 0 0 4 2 56.68 3.60 1.6240 3 3 0 4 56.86 5.33 1.6193 4 1 0 4 57.44 4.93 1.6043 3 1 2 4 57.81 7.12 1.5949 -2 1 4 4 58.15 4.18 1.5864 0 1 4 4 58.57 2.62 1.5761 -3 3 2 4 58.57 6.71 1.5759 2 4 0 4 58.89 1.97 1.5682 0 4 2 4 58.99 2.76 1.5658 2 3 2 4 60.82 2.18 1.5230 -1 2 4 4 62.26 4.94 1.4911 -2 4 2 4 62.44 3.59 1.4873 2 2 3 4 62.96 3.67 1.4763 -3 1 4 4 66.87 1.64 1.3991 4 2 1 4 66.91 1.85 1.3984 0 5 1 4 66.94 2.48 1.3978 -1 4 3 4 67.74 1.48 1.3833 3 0 3 2 67.98 5.11 1.3790 1 2 4 4 68.19 5.08 1.3753 -1 3 4 4 69.35 5.24 1.3550 3 3 2 4 69.68 1.05 1.3494 -2 3 4 4 69.99 1.39 1.3442 0 3 4 4 70.68 3.01 1.3327 2 0 4 2 71.17 4.34 1.3248 -4 1 4 4 71.23 2.42 1.3239 4 1 2 4 71.54 1.34 1.3189 3 4 1 4 71.78 1.25 1.3151 -2 5 1 4 71.78 1.36 1.3150 2 5 0 4 72.07 4.51 1.3105 0 5 2 4 72.11 1.59 1.3099 1 4 3 4 72.26 2.63 1.3075 5 1 0 4 74.39 5.43 1.2752 -3 3 4 4 74.49 1.03 1.2738 -3 0 5 2 74.72 5.72 1.2705 -5 2 2 4 74.87 1.02 1.2682 -3 4 3 4 74.99 1.03 1.2665 1 3 4 4 75.13 1.80 1.2645 -2 5 2 4 76.19 1.05 1.2495 -2 2 5 4 76.40 1.12 1.2466 5 2 0 4 78.14 1.24 1.2231 0 2 5 4 78.52 3.27 1.2182 -4 4 2 4 78.53 1.46 1.2180 4 4 0 4 79.64 1.33 1.2038 0 4 4 4 81.71 3.73 1.1785 2 5 2 4 82.06 2.15 1.1744 1 6 0 4 82.12 1.43 1.1736 -5 1 4 4 83.15 3.04 1.1617 5 3 0 4 84.90 1.97 1.1421 -6 0 2 2 86.70 1.00 1.1230 2 6 0 4 86.74 1.23 1.1226 -4 2 5 4 86.81 1.18 1.1219 4 2 3 4 87.29 2.59 1.1170 3 2 4 4 89.48 2.12 1.0952 6 1 0 4 89.56 1.21 1.0945 3 4 3 4 89.92 1.09 1.0910 2 6 1 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.