As2O(SO4)2 Mercier R, Douglade J Acta Crystallographica B38 (1982) 1731-1735 Structure cristalline d'un oxysulfate d'arsenic(III) As2O(SO4)2 (ou As2O3*(SO3)2) Note: AnisoB's from ICSD _database_code_amcsd 0009768 6.650 6.671 16.612 90 94.34 90 Pc atom x y z Biso B(1,1) B(2,2) B(3,3) B(1,2) B(1,3) B(2,3) As1 0 .0159 0 .95 .0060 .0051 .0009 .0005 .0005 -.0002 As2 -.1277 -.1357 .1670 1.08 .0082 .0050 .0010 .0001 .0000 .0002 As3 .5030 .3809 .2535 .97 .0074 .0044 .0010 -.0004 .0001 -.0003 As4 .3974 .5158 .4298 .98 .0064 .0056 .0009 -.0009 .0006 -.0002 S1 -.4472 -.0246 .0319 1.33 .0066 .0069 .0012 .0016 -.0002 .0000 S2 -.0288 .3260 .1390 1.52 .0119 .0061 .0013 -.0003 .0008 -.0005 S3 .8461 .4760 .3902 1.11 .0046 .0066 .0010 -.001 .0004 -.0002 S4 .419 .8213 .2876 1.35 .0085 .0063 .0011 .0002 .0000 .0003 O1 .0390 -.1224 .0872 .78 .0080 .0050 .0004 .0013 -.0004 .0010 O2 .3810 .3648 .3413 .98 .0041 .0049 .0011 .0012 .0000 -.0004 O11 -.2794 .0194 -.0194 2.73 .0126 .0233 .0018 -.0054 .0000 .0041 O12 -.3645 -.1008 .1177 4.22 .0135 .0405 .0036 .0006 -.0009 .0051 O13 -.5817 -.1753 -.0020 3.65 .0326 .0161 .0029 -.0106 -.0001 -.0028 O14 -.5114 .1749 .0499 1.33 .0122 .0043 .0018 .0046 .0024 .0002 O21 -.0122 .2613 .053 1.30 .0268 .0006 .0007 -.0009 .0025 .0000 O22 -.0893 .1482 .1916 2.46 .0319 .0029 .0024 .0009 .0023 -.0017 O23 -.2058 .4633 .1385 4.91 .0369 .0205 .0045 .0061 .0015 .0019 O24 .1676 .3416 .1713 4.01 .0093 .0357 .0033 -.0051 -.0002 .0003 O31 .7613 .3569 .3203 1.13 .0060 .0082 .0007 .0015 -.0002 -.0015 O32 .6674 .4741 .4466 1.05 .0049 .0063 .0011 .0016 .0005 -.0003 O33 .9969 .3580 .4321 1.76 .0114 .0065 .0018 .0003 -.0004 .0005 O34 .9468 .6486 .3724 4.95 .049 .0107 .0047 -.0118 .0078 -.0018 O41 .5406 .6474 .2470 1.65 .0158 .0020 .0023 .0007 -.0018 .0004 O42 .4134 .7571 .3737 3.10 .0491 .0052 .0012 .0013 .0032 .0006 O43 .5544 .9833 .2881 1.07 .0055 .0036 .0014 -.0003 .0006 .0003 O44 .2316 .8976 .2551 4.98 .0085 .058 .0046 .0030 -.0021 .0037