FeS King H E, Prewitt C T Acta Crystallographica B38 (1982) 1877-1887 High-pressure and high-temperature polymorphism of iron sulfides (FeS) Sample: T = 463 K, P = 0.0001 GPa, MnP-type structure _database_code_amcsd 0009772 CELL PARAMETERS: 5.8250 3.4675 6.0059 90.000 90.000 90.000 SPACE GROUP: Pnma X-RAY WAVELENGTH: 1.541838 Cell Volume: 121.308 Density (g/cm3): 4.813 MAX. ABS. INTENSITY / VOLUME**2: 71.35855327 RIR: 4.828 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 29.75 15.60 3.0029 0 0 2 2 29.75 34.23 3.0029 0 1 1 4 30.70 5.50 2.9125 2 0 0 2 33.58 11.51 2.6691 1 0 2 4 33.58 23.49 2.6691 1 1 1 8 42.75 1.88 2.1151 1 1 2 8 43.28 33.54 2.0907 2 0 2 4 43.28 66.46 2.0907 2 1 1 8 48.06 1.08 1.8933 1 0 3 4 52.80 23.31 1.7338 0 1 3 4 52.80 12.26 1.7337 0 2 0 2 56.43 1.74 1.6305 3 0 2 4 56.43 3.92 1.6305 3 1 1 8 61.79 1.14 1.5015 0 0 4 2 61.79 2.36 1.5015 0 2 2 4 62.33 1.36 1.4898 2 1 3 8 63.93 5.71 1.4562 4 0 0 2 64.04 1.26 1.4539 1 0 4 4 64.04 2.41 1.4539 1 2 2 8 70.57 4.40 1.3346 2 0 4 4 70.57 10.20 1.3346 2 2 2 8 72.08 1.18 1.3103 4 0 2 4 72.08 2.61 1.3103 4 1 1 8 80.94 1.02 1.1878 3 2 2 8 87.47 6.74 1.1151 4 1 3 8 87.47 3.53 1.1151 4 2 0 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.