FeS King H E, Prewitt C T Acta Crystallographica B38 (1982) 1877-1887 High-pressure and high-temperature polymorphism of iron sulfides (FeS) Sample: T = 294 K, P = 4.15 GPa, MnP-type structure Note: a cell edge altered from value reported _database_code_amcsd 0009773 CELL PARAMETERS: 5.7160 3.3470 5.7970 90.000 90.000 90.000 SPACE GROUP: Pnma X-RAY WAVELENGTH: 1.541838 Cell Volume: 110.905 Density (g/cm3): 5.264 MAX. ABS. INTENSITY / VOLUME**2: 74.04135654 RIR: 4.580 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 21.84 6.13 4.0702 1 0 1 4 30.85 35.88 2.8986 0 1 1 4 30.85 10.27 2.8985 0 0 2 2 31.30 7.49 2.8580 2 0 0 2 34.70 23.98 2.5852 1 1 1 8 34.70 12.28 2.5851 1 0 2 4 41.55 2.55 2.1734 2 1 0 4 44.27 17.82 2.0459 1 1 2 8 44.52 68.82 2.0351 2 1 1 8 44.52 31.18 2.0351 2 0 2 4 49.81 9.12 1.8306 1 0 3 4 50.42 4.16 1.8101 3 0 1 4 54.86 13.94 1.6735 0 2 0 2 54.86 17.35 1.6735 0 1 3 4 57.92 4.14 1.5922 3 1 1 8 64.27 1.77 1.4493 0 2 2 4 64.53 1.32 1.4441 2 2 0 4 65.30 6.00 1.4290 4 0 0 2 66.56 2.70 1.4048 1 2 2 8 66.57 1.30 1.4048 1 0 4 4 69.25 2.30 1.3567 3 0 3 4 73.05 4.96 1.2953 1 1 4 8 73.23 10.45 1.2926 2 2 2 8 73.23 1.61 1.2926 2 0 4 4 73.95 4.01 1.2817 4 1 1 8 73.95 1.25 1.2817 4 0 2 4 77.24 3.57 1.2351 1 2 3 8 77.71 1.81 1.2288 3 2 1 8 85.45 2.55 1.1363 1 0 5 4 89.97 5.41 1.0905 3 1 4 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.