Zr0.935Y0.065O1.968 Howard C J, Hill R J, Reichert B E Acta Crystallographica B44 (1988) 116-120 Structures of the ZrO2 polymorphs at room temperature by high-resolution neutron powder diffraction Locality: synthetic _database_code_amcsd 0019230 CELL PARAMETERS: 3.6055 3.6055 5.1797 90.000 90.000 90.000 SPACE GROUP: P4_2/nmc X-RAY WAVELENGTH: 1.541838 Cell Volume: 67.334 Density (g/cm3): 10.535 MAX. ABS. INTENSITY / VOLUME**2: 223.1804665 RIR: 6.898 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 34.64 42.83 2.5898 0 0 2 2 35.20 77.56 2.5495 1 1 0 4 50.21 100.00 1.8169 1 1 2 8 50.64 50.35 1.8027 2 0 0 4 62.80 29.20 1.4796 2 0 2 8 73.07 6.44 1.2949 0 0 4 2 74.42 13.56 1.2747 2 2 0 4 83.78 13.69 1.1545 1 1 4 8 84.76 12.20 1.1437 2 2 2 8 85.09 11.70 1.1402 3 1 0 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.