Mutinaite van Koningsveld H Acta Crystallographica B46 (1990) 731-735 High-temperature (350 K) orthorhombic framework structure of zeolite H-ZSM-5 Locality: synthetic Note: anisotropic thermal parameters obtained from ICSD _database_code_amcsd 0009842 CELL PARAMETERS: 20.0780 19.8940 13.3720 90.000 90.000 90.000 SPACE GROUP: Pnma X-RAY WAVELENGTH: 1.541838 Cell Volume: 5341.201 Density (g/cm3): 1.793 MAX. ABS. INTENSITY / VOLUME**2: 11.59796345 RIR: 2.106 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 7.94 100.00 11.1296 1 0 1 4 7.97 72.33 11.0979 0 1 1 4 8.81 46.95 10.0390 2 0 0 2 8.89 50.89 9.9470 0 2 0 2 9.10 24.43 9.7129 1 1 1 8 9.87 1.54 8.9625 2 1 0 4 11.93 1.43 7.4166 1 2 1 8 13.24 6.24 6.6860 0 0 2 2 13.96 13.72 6.3435 1 0 2 4 14.80 14.41 5.9849 3 0 1 4 14.91 8.58 5.9409 0 3 1 4 15.55 9.05 5.6968 1 3 1 8 15.93 7.40 5.5648 2 0 2 4 15.97 4.64 5.5490 0 2 2 4 16.02 1.40 5.5332 2 3 0 4 16.57 2.94 5.3485 1 2 2 8 17.29 1.41 5.1282 3 2 1 8 17.67 3.81 5.0195 4 0 0 2 17.83 5.86 4.9735 0 4 0 2 19.29 3.58 4.6018 3 1 2 8 20.41 1.55 4.3514 1 0 3 4 20.42 3.05 4.3495 0 1 3 4 20.84 1.45 4.2627 2 3 2 8 20.91 6.71 4.2490 4 2 1 8 21.82 1.24 4.0738 2 0 3 4 22.21 2.55 4.0022 4 3 0 4 23.10 1.68 3.8508 3 3 2 8 23.13 45.55 3.8459 5 0 1 4 23.33 37.16 3.8136 0 5 1 4 23.75 15.66 3.7466 1 5 1 8 23.99 23.16 3.7099 3 0 3 4 24.06 1.84 3.6993 0 3 3 4 24.06 1.05 3.6989 2 5 0 4 24.47 18.77 3.6381 1 3 3 8 24.82 1.33 3.5871 5 2 1 8 25.63 2.03 3.4760 3 2 3 8 25.95 6.03 3.4340 4 3 2 8 26.27 1.45 3.3920 5 1 2 8 26.44 1.11 3.3706 1 5 2 8 26.64 2.41 3.3463 6 0 0 2 26.75 1.75 3.3329 4 0 3 4 26.89 2.56 3.3157 0 6 0 2 27.04 5.01 3.2976 1 0 4 4 27.56 1.15 3.2366 2 5 2 8 28.13 1.01 3.1718 2 0 4 4 28.52 1.75 3.1301 1 2 4 8 29.33 6.17 3.0448 3 5 2 8 29.95 5.08 2.9834 5 0 3 4 30.11 5.16 2.9683 0 5 3 4 30.44 4.76 2.9363 1 5 3 8 31.30 1.35 2.8577 5 2 3 8 32.84 2.88 2.7276 6 3 2 8 34.45 3.23 2.6033 5 5 2 8 34.73 1.04 2.5830 7 3 1 8 35.78 1.93 2.5097 8 0 0 2 36.12 1.30 2.4867 0 8 0 2 36.17 1.22 2.4835 3 0 5 4 36.22 1.09 2.4803 0 3 5 4 37.28 1.72 2.4120 7 0 3 4 37.61 1.13 2.3916 6 5 2 8 37.63 1.52 2.3906 3 5 4 8 37.81 1.22 2.3795 1 7 3 8 38.82 1.07 2.3195 4 7 2 8 45.16 2.97 2.0078 10 0 0 2 45.18 3.32 2.0071 8 0 4 4 45.46 1.36 1.9953 0 8 4 4 45.51 1.75 1.9931 4 8 3 8 45.60 4.16 1.9894 0 10 0 2 45.69 1.12 1.9855 1 8 4 8 46.65 1.74 1.9471 4 3 6 8 47.60 1.04 1.9104 9 3 3 8 48.77 1.92 1.8672 3 5 6 8 55.11 1.36 1.6665 8 0 6 4 55.56 1.39 1.6540 1 8 6 8 62.45 1.65 1.4872 9 8 4 8 63.78 3.03 1.4593 13 0 3 4 64.22 1.73 1.4503 4 8 7 8 64.55 2.66 1.4436 1 13 3 8 65.25 1.41 1.4299 4 13 2 8 65.76 2.05 1.4200 8 5 7 8 66.42 1.15 1.4075 13 5 2 8 67.26 1.17 1.3919 0 5 9 4 79.25 1.43 1.2087 5 5 10 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.