Fe2 O5 P Elkaim E, Berar J, Gleitzer C, Malaman B, Ijjaali M, Lecomte C Acta Crystallographica B52 (1996) 428-431 Occurrence of a monoclinic distortion in beta-Fe2 P O5 _cod_database_code 1008736 _database_code_amcsd 0016617 CELL PARAMETERS: 7.2956 7.5605 7.2512 90.000 117.368 90.000 SPACE GROUP: I2/a X-RAY WAVELENGTH: 1.541838 Cell Volume: 355.197 Density (g/cm3): 4.163 MAX. ABS. INTENSITY / VOLUME**2: 21.43122383 RIR: 1.676 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.03 33.17 4.9197 1 1 0 4 18.10 31.24 4.9024 0 1 1 4 27.17 97.82 3.2822 -2 1 1 4 27.30 100.00 3.2668 -1 1 2 4 27.53 14.36 3.2395 2 0 0 2 27.62 28.09 3.2295 -1 2 1 4 27.71 12.15 3.2198 0 0 2 2 28.73 28.08 3.1068 -2 0 2 2 33.52 13.30 2.6731 1 2 1 4 36.53 20.94 2.4598 2 2 0 4 36.66 22.05 2.4512 0 2 2 4 38.29 16.05 2.3507 2 1 1 4 38.32 16.47 2.3487 1 3 0 4 38.35 13.38 2.3468 0 3 1 4 38.39 11.83 2.3450 1 1 2 4 39.93 5.18 2.2580 -3 1 2 4 40.08 5.19 2.2496 -2 1 3 4 43.58 14.92 2.0766 3 1 0 4 43.67 14.87 2.0727 -2 3 1 4 43.76 15.24 2.0688 -1 3 2 4 43.84 14.63 2.0649 0 1 3 4 44.61 5.29 2.0312 -3 2 1 4 44.84 4.60 2.0214 -1 2 3 4 48.14 16.13 1.8902 2 0 2 2 48.14 16.11 1.8901 0 4 0 2 50.23 2.61 1.8164 -3 2 3 4 50.38 1.90 1.8112 -2 0 4 2 51.79 3.38 1.7652 2 3 1 4 51.87 2.34 1.7628 1 3 2 4 54.37 5.90 1.6873 -4 1 3 4 54.54 4.71 1.6824 -3 1 4 4 56.04 22.78 1.6411 -4 2 2 4 56.08 11.41 1.6399 3 3 0 4 56.30 10.08 1.6341 0 3 3 4 56.31 1.91 1.6339 3 2 1 4 56.32 24.97 1.6334 -2 2 4 4 56.36 1.85 1.6326 2 4 0 4 56.45 2.04 1.6300 0 4 2 4 56.50 1.77 1.6288 1 2 3 4 56.84 16.48 1.6198 4 0 0 2 57.03 30.18 1.6148 -2 4 2 4 57.22 13.87 1.6099 0 0 4 2 59.51 5.57 1.5534 -4 0 4 2 63.09 2.57 1.4735 3 1 2 4 63.14 1.95 1.4725 1 5 0 4 63.16 2.64 1.4721 0 5 1 4 63.20 2.23 1.4712 2 1 3 4 64.16 1.32 1.4516 -4 3 1 4 64.49 1.52 1.4449 -1 3 4 4 65.25 4.56 1.4298 -5 1 2 4 65.41 4.89 1.4268 -4 3 3 4 65.56 4.27 1.4239 -3 3 4 4 65.71 4.92 1.4209 -2 1 5 4 66.88 2.16 1.3990 4 1 1 4 67.01 2.11 1.3966 -2 5 1 4 67.07 2.58 1.3954 -1 5 2 4 67.20 2.71 1.3931 1 1 4 4 70.23 1.03 1.3403 -3 2 5 4 70.33 1.42 1.3385 -5 1 4 4 70.45 21.63 1.3365 2 4 2 4 71.87 1.11 1.3137 -5 2 1 4 71.99 1.31 1.3117 -4 4 2 4 72.37 1.06 1.3058 -1 2 5 4 75.82 1.22 1.2547 -2 3 5 4 76.92 2.80 1.2395 4 3 1 4 76.98 2.77 1.2387 3 5 0 4 77.16 3.25 1.2362 0 5 3 4 77.22 3.40 1.2354 1 3 4 4 77.63 2.47 1.2299 4 4 0 4 77.96 1.85 1.2256 0 4 4 4 80.20 1.89 1.1968 -5 3 4 4 80.38 1.44 1.1946 -4 3 5 4 81.98 1.74 1.1753 4 2 2 4 82.06 1.83 1.1744 2 6 0 4 82.14 2.23 1.1734 0 6 2 4 82.22 2.29 1.1725 2 2 4 4 85.21 2.49 1.1388 -4 5 3 4 85.35 2.01 1.1373 -3 5 4 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.