KCr(SO4)2*12H2O Nyburg S C, Steed J, Aleksovska S, Petrusevski V M Acta Crystallographica B56 (2000) 204-209 Structure of the alums. I. On the sulfate group disorder in the alpha-alums Sample: T = 173 K _database_code_amcsd 0009914 CELL PARAMETERS: 12.2133 12.2133 12.2133 90.000 90.000 90.000 SPACE GROUP: Pa3 X-RAY WAVELENGTH: 1.541838 Cell Volume: 1821.793 Density (g/cm3): 1.821 MAX. ABS. INTENSITY / VOLUME**2: 9.059542309 RIR: 1.620 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 12.55 26.84 7.0514 1 1 1 8 14.51 3.32 6.1066 2 0 0 6 16.23 24.94 5.4620 2 1 0 12 17.79 12.05 4.9861 2 1 1 24 20.57 100.00 4.3181 2 2 0 12 21.83 35.46 4.0711 2 2 1 24 24.17 23.12 3.6824 3 1 1 24 25.26 2.66 3.5257 2 2 2 8 26.31 1.18 3.3874 3 0 2 12 27.32 15.88 3.2641 3 2 1 24 27.32 37.22 3.2641 3 1 2 24 29.25 36.40 3.0533 4 0 0 6 30.17 10.83 2.9622 4 1 0 12 30.17 2.00 2.9622 3 2 2 24 31.07 6.76 2.8787 4 1 1 24 31.94 16.39 2.8019 3 3 1 24 32.79 20.63 2.7310 4 2 0 12 33.63 6.41 2.6652 4 1 2 24 34.44 7.61 2.6039 3 3 2 24 36.03 12.16 2.4930 4 2 2 24 37.55 2.36 2.3952 4 3 1 24 38.29 2.43 2.3505 5 1 1 24 38.29 4.43 2.3505 3 3 3 8 39.74 2.14 2.2680 4 3 2 24 40.45 3.62 2.2298 5 1 2 24 41.84 5.00 2.1590 4 4 0 12 42.52 4.15 2.1261 4 4 1 24 43.19 1.30 2.0946 4 3 3 24 43.85 6.76 2.0644 5 1 3 24 44.51 10.35 2.0355 6 0 0 6 45.16 5.04 2.0079 6 1 0 12 45.80 1.97 1.9813 6 1 1 24 45.80 4.24 1.9813 5 3 2 24 47.06 17.23 1.9311 6 0 2 12 47.06 6.92 1.9311 6 2 0 12 48.90 2.02 1.8625 5 3 3 24 49.50 3.41 1.8412 6 2 2 24 50.10 1.54 1.8207 5 4 2 24 50.70 3.84 1.8008 6 3 1 24 53.02 1.23 1.7272 5 4 3 24 53.59 4.73 1.7102 7 1 1 24 54.15 1.23 1.6937 6 0 4 12 54.15 5.89 1.6937 6 4 0 12 54.71 1.10 1.6776 6 4 1 24 56.37 5.61 1.6321 6 4 2 24 56.37 6.05 1.6321 6 2 4 24 56.92 3.73 1.6177 7 2 2 24 58.00 1.21 1.5900 7 3 1 24 58.00 2.06 1.5900 5 5 3 24 59.61 1.09 1.5511 6 5 1 24 61.70 1.21 1.5034 7 1 4 24 62.73 3.28 1.4811 8 0 2 12 62.73 2.84 1.4811 8 2 0 12 63.25 1.12 1.4703 7 2 4 24 64.77 4.83 1.4394 6 6 0 12 65.77 1.13 1.4198 7 4 3 24 66.27 2.37 1.4103 7 1 5 24 66.77 1.79 1.4010 6 6 2 24 68.75 1.42 1.3655 8 0 4 12 69.23 2.74 1.3570 8 4 1 24 71.18 1.10 1.3247 7 0 6 12 72.62 2.84 1.3019 6 6 4 24 73.09 1.04 1.2946 9 2 2 24 76.41 1.25 1.2465 8 4 4 24 80.14 3.78 1.1976 8 6 2 24 80.14 1.61 1.1976 8 2 6 24 81.99 1.03 1.1752 6 6 6 8 88.41 1.08 1.1057 9 4 5 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.