Lanmuchangite Nyburg S C, Steed J, Aleksovska S, Petrusevski V M Acta Crystallographica B56 (2000) 204-209 Structure of the alums. I. On the sulfate group disorder in the alpha-alums Locality: synthetic Sample: T = 173 K _database_code_amcsd 0009916 CELL PARAMETERS: 12.2070 12.2070 12.2070 90.000 90.000 90.000 SPACE GROUP: Pa3 X-RAY WAVELENGTH: 1.541838 Cell Volume: 1818.975 Density (g/cm3): 2.336 MAX. ABS. INTENSITY / VOLUME**2: 34.77800600 RIR: 4.849 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 12.56 43.85 7.0477 1 1 1 8 14.51 35.85 6.1035 2 0 0 6 16.24 6.62 5.4591 2 1 0 12 17.80 4.13 4.9835 2 1 1 24 20.58 100.00 4.3158 2 2 0 12 21.84 8.80 4.0690 2 2 1 24 24.18 28.44 3.6805 3 1 1 24 25.27 17.11 3.5239 2 2 2 8 27.34 3.90 3.2625 3 2 1 24 27.34 10.03 3.2625 3 1 2 24 29.26 26.75 3.0517 4 0 0 6 30.19 2.76 2.9606 4 1 0 12 31.08 1.64 2.8772 4 1 1 24 31.96 57.31 2.8005 3 3 1 24 32.81 7.29 2.7296 4 0 2 12 32.81 25.41 2.7296 4 2 0 12 33.64 1.48 2.6638 4 1 2 24 34.46 2.14 2.6025 3 3 2 24 36.04 26.34 2.4917 4 2 2 24 38.31 13.09 2.3492 5 1 1 24 38.31 11.44 2.3492 3 3 3 8 41.86 8.18 2.1579 4 4 0 12 42.54 1.02 2.1250 4 4 1 24 43.88 9.19 2.0634 5 3 1 24 43.88 4.47 2.0634 5 1 3 24 44.53 7.88 2.0345 6 0 0 6 44.53 6.96 2.0345 4 4 2 24 45.18 1.36 2.0068 6 1 0 12 47.08 13.91 1.9301 6 0 2 12 47.08 7.65 1.9301 6 2 0 12 48.93 13.50 1.8615 5 3 3 24 49.53 8.63 1.8403 6 2 2 24 51.89 1.90 1.7619 4 4 4 8 53.62 1.39 1.7093 7 1 1 24 53.62 4.48 1.7093 5 5 1 24 54.18 3.08 1.6928 6 0 4 12 54.18 5.78 1.6928 6 4 0 12 56.41 8.16 1.6312 6 4 2 24 56.41 8.71 1.6312 6 2 4 24 56.95 1.05 1.6169 7 2 2 24 58.04 2.14 1.5892 7 3 1 24 58.04 5.23 1.5892 7 1 3 24 58.04 2.24 1.5892 5 5 3 24 62.25 1.99 1.4913 7 3 3 24 62.77 3.82 1.4803 8 0 2 12 62.77 3.52 1.4803 8 2 0 12 62.77 3.11 1.4803 6 4 4 24 64.81 2.69 1.4386 8 2 2 24 64.81 4.06 1.4386 6 6 0 12 66.31 1.48 1.4095 7 5 1 24 66.81 3.25 1.4002 6 6 2 24 68.79 2.08 1.3648 8 0 4 12 68.79 1.78 1.3648 8 4 0 12 70.25 2.15 1.3399 7 5 3 24 70.25 2.36 1.3399 7 3 5 24 70.25 1.59 1.3399 9 1 1 24 70.73 1.66 1.3319 8 4 2 24 70.73 2.31 1.3319 8 2 4 24 72.66 3.30 1.3013 6 6 4 24 74.09 2.01 1.2796 9 3 1 24 74.09 1.56 1.2796 9 1 3 24 76.45 2.42 1.2459 8 4 4 24 77.86 1.08 1.2268 9 3 3 24 80.19 3.74 1.1970 8 6 2 24 80.19 2.41 1.1970 8 2 6 24 82.04 1.36 1.1746 10 2 2 24 82.04 1.03 1.1746 6 6 6 8 85.26 1.30 1.1383 9 5 3 24 85.26 1.40 1.1383 9 3 5 24 85.72 1.01 1.1334 8 6 4 24 85.72 1.40 1.1334 8 4 6 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.