Ca2Co.9Zn.1Si2O7 Jia Z H, Schaper A K, Massa W, Treutmann W, Rager H Acta Crystallographica B62 (2006) 547-555 Structure and phase transitions in Ca2CoSi2O7-Ca2ZnSi2O7 solid-solution crystals _database_code_amcsd 0009940 CELL PARAMETERS: 23.5180 23.5180 5.0263 90.000 90.000 90.000 SPACE GROUP: P-4 X-RAY WAVELENGTH: 1.541838 Cell Volume: 2780.028 Density (g/cm3): 3.310 MAX. ABS. INTENSITY / VOLUME**2: 20.52327889 RIR: 2.019 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 15.99 1.02 5.5432 3 3 0 4 17.65 17.60 5.0263 0 0 1 2 21.00 6.60 4.2313 3 0 1 4 23.90 38.45 3.7235 3 3 1 4 25.41 2.33 3.5059 3 6 0 4 25.41 1.44 3.5059 6 3 0 4 28.89 59.64 3.0909 6 0 1 4 31.10 45.94 2.8755 3 6 1 4 31.10 54.06 2.8755 6 3 1 4 32.30 12.23 2.7716 6 6 0 4 35.73 6.23 2.5131 0 0 2 2 36.24 16.43 2.4790 9 3 0 4 36.24 18.91 2.4790 3 9 0 4 37.04 11.29 2.4271 6 6 1 4 37.58 6.33 2.3932 3 0 2 4 38.84 6.75 2.3185 9 0 1 4 39.37 4.96 2.2889 3 3 2 4 40.58 4.85 2.2233 9 3 1 4 40.58 3.00 2.2233 3 9 1 4 44.35 5.36 2.0426 3 6 2 4 44.35 5.83 2.0426 6 3 2 4 46.33 1.41 1.9598 12 0 0 4 47.84 2.22 1.9013 3 12 0 4 47.84 3.01 1.9013 12 3 0 4 48.92 10.01 1.8618 6 6 2 4 49.32 3.71 1.8477 9 9 0 4 49.95 2.29 1.8259 12 0 1 4 51.38 4.08 1.7783 12 3 1 4 51.38 4.06 1.7783 3 12 1 4 51.80 14.06 1.7649 9 3 2 4 51.80 18.19 1.7649 3 9 2 4 52.18 6.88 1.7529 12 6 0 4 52.18 5.20 1.7529 6 12 0 4 52.79 7.49 1.7343 9 9 1 4 55.52 1.92 1.6552 12 6 1 4 55.52 2.53 1.6552 6 12 1 4 55.92 1.55 1.6443 6 9 2 4 57.46 4.04 1.6038 3 3 3 4 60.05 4.23 1.5406 6 0 3 4 60.19 1.23 1.5374 15 3 0 4 61.32 2.22 1.5117 3 6 3 4 61.32 2.43 1.5117 6 3 3 4 63.25 3.21 1.4702 15 3 1 4 63.25 3.95 1.4702 3 15 1 4 64.85 2.03 1.4377 6 12 2 4 64.85 2.10 1.4377 12 6 2 4 65.05 4.35 1.4338 6 6 3 4 66.27 2.07 1.4104 9 0 3 4 66.92 2.95 1.3983 15 6 1 4 66.92 3.13 1.3983 6 15 1 4 67.47 1.76 1.3881 9 3 3 4 67.47 1.34 1.3881 3 9 3 4 67.60 3.39 1.3858 12 12 0 4 70.49 3.64 1.3360 12 12 1 4 72.32 3.78 1.3066 18 0 0 4 75.66 1.68 1.2570 12 3 3 4 75.66 1.61 1.2570 3 12 3 4 75.69 1.71 1.2566 0 0 4 2 76.80 2.70 1.2412 9 9 3 4 79.67 1.28 1.2035 6 18 1 4 79.67 1.83 1.2035 18 6 1 4 81.13 1.39 1.1855 9 15 2 4 81.13 1.20 1.1855 15 9 2 4 83.37 2.34 1.1593 18 0 2 4 84.69 1.21 1.1444 6 6 4 4 85.77 1.40 1.1328 15 3 3 4 85.77 1.71 1.1328 3 15 3 4 86.92 1.42 1.1208 9 3 4 4 86.92 1.36 1.1208 3 9 4 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.