B2 Ca O10 U2 Gasperin M Acta Crystallographica C43 (1987) 1247-1250 Synthese et structure du borouranate de calcium: Ca B2 U2 O10. _cod_database_code 1001347 _database_code_amcsd 0010039 CELL PARAMETERS: 16.5120 8.1690 6.5820 90.000 96.970 90.000 SPACE GROUP: C2 X-RAY WAVELENGTH: 1.541838 Cell Volume: 881.262 Density (g/cm3): 5.258 MAX. ABS. INTENSITY / VOLUME**2: 101.4245126 RIR: 6.281 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 10.80 57.81 8.1950 2 0 0 2 12.11 50.11 7.3112 1 1 0 2 16.29 9.50 5.4405 -2 0 1 2 17.71 33.96 5.0082 -1 1 1 2 18.37 43.29 4.8308 2 0 1 2 18.70 7.05 4.7457 1 1 1 2 19.55 8.29 4.5413 3 1 0 2 21.76 100.00 4.0845 0 2 0 1 24.20 46.24 3.6780 -4 0 1 2 24.35 12.59 3.6556 2 2 0 2 24.98 9.27 3.5643 3 1 1 2 27.05 43.32 3.2959 4 0 1 2 27.30 27.53 3.2667 0 0 2 2 27.30 4.85 3.2664 -2 2 1 2 28.15 27.25 3.1697 -2 0 2 2 28.62 19.87 3.1190 2 2 1 2 29.34 11.02 3.0445 -1 1 2 2 29.36 8.40 3.0422 5 1 0 2 31.00 11.09 2.8850 -5 1 1 2 32.77 26.82 2.7332 -4 2 1 2 32.79 5.99 2.7317 6 0 0 2 33.36 2.97 2.6862 1 3 0 2 33.88 2.62 2.6462 5 1 1 2 34.00 10.48 2.6367 -6 0 1 2 34.98 30.04 2.5650 4 2 1 2 35.18 19.00 2.5511 0 2 2 2 35.43 4.94 2.5335 3 1 2 2 35.86 18.72 2.5041 -2 2 2 2 35.89 4.65 2.5020 -1 3 1 2 36.42 1.34 2.4672 1 3 1 2 36.88 1.54 2.4371 3 3 0 2 37.18 1.51 2.4180 6 0 1 2 38.08 5.77 2.3630 -5 1 2 2 39.69 5.51 2.2707 6 2 0 2 40.06 2.24 2.2508 7 1 0 2 40.19 1.92 2.2440 3 3 1 2 40.73 8.52 2.2152 -6 2 1 2 41.46 1.16 2.1778 0 0 3 2 42.67 2.09 2.1188 -1 1 3 2 42.84 2.40 2.1109 5 1 2 2 43.17 2.60 2.0953 -1 3 2 2 43.19 2.69 2.0946 5 3 0 2 43.49 1.66 2.0807 6 2 1 2 44.06 3.95 2.0555 7 1 1 2 44.21 9.77 2.0487 8 0 0 2 44.28 1.09 2.0458 -3 1 3 2 44.31 9.91 2.0441 2 0 3 2 44.36 16.65 2.0422 0 4 0 1 44.38 3.03 2.0411 -5 3 1 2 44.69 7.32 2.0277 -4 0 3 2 45.79 3.33 1.9816 2 4 0 2 45.81 5.56 1.9806 6 0 2 2 47.30 1.52 1.9217 0 2 3 2 47.56 1.08 1.9120 -2 4 1 2 47.75 1.83 1.9046 3 3 2 2 48.13 3.72 1.8907 3 1 3 2 48.39 6.06 1.8811 2 4 1 2 48.60 1.99 1.8735 -5 1 3 2 49.57 4.58 1.8390 -8 0 2 2 49.74 3.53 1.8331 4 0 3 2 49.79 9.75 1.8313 8 2 0 2 49.86 2.21 1.8289 -5 3 2 2 49.89 10.41 1.8279 2 2 3 2 50.23 7.77 1.8162 -4 2 3 2 50.31 7.08 1.8135 -6 0 3 2 51.16 10.49 1.7855 -4 4 1 2 51.26 6.11 1.7821 6 2 2 2 51.41 2.89 1.7775 9 1 0 2 51.67 4.32 1.7690 -9 1 1 2 51.96 3.09 1.7600 7 1 2 2 52.73 11.38 1.7360 4 4 1 2 52.87 7.81 1.7317 0 4 2 2 53.37 7.62 1.7168 -2 4 2 2 53.79 1.05 1.7042 5 3 2 2 54.74 4.83 1.6769 -8 2 2 2 54.82 1.64 1.6747 7 3 1 2 54.90 4.19 1.6724 4 2 3 2 55.13 1.22 1.6659 9 1 1 2 55.44 7.37 1.6575 -6 2 3 2 55.78 3.43 1.6480 8 0 2 2 55.88 1.85 1.6453 -9 1 2 2 56.06 4.92 1.6404 -2 0 4 2 56.12 1.58 1.6390 10 0 0 2 56.24 2.16 1.6357 6 4 0 2 56.33 1.19 1.6333 0 0 4 2 56.61 1.04 1.6257 1 5 0 2 57.04 3.96 1.6146 -6 4 1 2 58.32 1.21 1.5821 -1 5 1 2 58.33 1.61 1.5819 3 3 3 2 59.82 1.07 1.5461 10 0 1 2 60.00 2.39 1.5419 -10 0 2 2 60.59 4.40 1.5283 8 2 2 2 60.85 5.66 1.5223 -2 2 4 2 60.90 2.00 1.5211 10 2 0 2 61.11 1.63 1.5166 0 2 4 2 61.23 1.36 1.5138 9 3 0 2 61.47 2.17 1.5085 -9 3 1 2 61.72 1.46 1.5029 7 3 2 2 62.32 1.11 1.4898 3 1 4 2 62.73 1.19 1.4811 7 1 3 2 62.90 1.24 1.4775 -4 2 4 2 63.62 1.18 1.4625 -1 5 2 2 64.42 4.98 1.4464 8 4 0 2 64.44 1.41 1.4460 10 2 1 2 64.50 5.34 1.4447 2 4 3 2 64.55 1.38 1.4437 -5 5 1 2 64.61 2.73 1.4425 -10 2 2 2 64.79 3.58 1.4389 -4 4 3 2 65.67 3.05 1.4218 6 4 2 2 68.45 1.49 1.3707 -12 0 1 2 68.68 2.93 1.3666 -8 4 2 2 68.82 2.17 1.3642 4 4 3 2 68.98 2.76 1.3615 0 6 0 1 69.29 4.43 1.3560 -6 4 3 2 70.70 1.40 1.3324 6 0 4 2 72.07 1.28 1.3104 2 6 1 2 72.78 1.93 1.2994 -12 2 1 2 73.90 2.59 1.2825 8 4 2 2 74.14 3.55 1.2789 -2 4 4 2 74.18 1.23 1.2783 10 4 0 2 74.28 2.40 1.2768 -4 6 1 2 74.97 2.06 1.2667 6 2 4 2 74.98 1.65 1.2667 2 0 5 2 75.56 2.78 1.2584 4 6 1 2 75.68 1.96 1.2567 0 6 2 2 76.09 1.85 1.2510 -2 6 2 2 76.55 1.16 1.2445 0 2 5 2 76.62 1.39 1.2436 12 2 1 2 76.98 1.37 1.2387 -6 0 5 2 77.31 1.19 1.2342 -10 0 4 2 77.58 1.92 1.2305 -10 4 2 2 79.17 2.43 1.2098 2 2 5 2 79.18 1.06 1.2097 -6 6 1 2 81.09 1.51 1.1859 10 2 3 2 81.13 1.82 1.1854 -6 2 5 2 81.46 1.50 1.1815 -10 2 4 2 85.28 1.42 1.1381 -12 4 1 2 85.67 1.58 1.1339 8 6 0 2 85.74 1.83 1.1331 2 6 3 2 85.91 1.25 1.1314 -14 2 1 2 86.00 1.12 1.1303 -4 6 3 2 86.80 1.07 1.1220 6 6 2 2 87.39 1.43 1.1159 6 4 4 2 88.99 1.06 1.1000 12 4 1 2 89.58 1.09 1.0942 -8 6 2 2 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.