Na2CaGe2O6 Nishi F, Takeuchi Y Acta Crystallographica C46 (1990) 544-546 Structure of sodium calcium germanate Na2CaGe2O6 _database_code_amcsd 0010123 CELL PARAMETERS: 10.7880 10.7880 13.4600 90.000 90.000 120.000 SPACE GROUP: R-3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 1356.618 Density (g/cm3): 3.606 MAX. ABS. INTENSITY / VOLUME**2: 25.04135529 RIR: 2.261 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 11.53 1.43 7.6750 1 0 1 6 16.23 15.00 5.4607 0 1 2 6 16.43 23.39 5.3940 1 1 0 6 19.79 10.10 4.4867 0 0 3 2 20.12 8.47 4.4131 0 2 1 6 23.18 97.11 3.8375 2 0 2 6 25.83 11.79 3.4494 1 1 3 12 26.09 37.24 3.4156 2 1 1 12 28.19 5.95 3.1659 1 0 4 6 28.55 8.01 3.1269 1 2 2 12 28.66 10.30 3.1142 3 0 0 6 32.80 99.01 2.7304 0 2 4 6 33.22 100.00 2.6970 2 2 0 6 34.68 1.69 2.5868 0 1 5 6 35.08 3.63 2.5583 3 0 3 6 35.27 3.05 2.5445 1 3 1 12 36.90 2.98 2.4361 2 1 4 12 38.60 10.64 2.3324 2 0 5 6 38.96 1.66 2.3115 2 2 3 12 40.20 1.07 2.2433 0 0 6 2 42.72 9.88 2.1167 3 2 1 12 44.36 2.35 2.0423 2 3 2 12 47.38 43.87 1.9188 4 0 4 6 48.33 3.61 1.8834 1 0 7 6 49.08 11.12 1.8561 1 4 3 12 49.08 1.43 1.8561 4 1 3 12 49.23 10.22 1.8508 0 5 1 6 50.11 1.64 1.8202 0 3 6 6 51.39 7.50 1.7781 0 2 7 6 51.82 2.30 1.7642 0 4 5 6 53.10 5.48 1.7247 2 2 6 12 53.67 6.78 1.7078 4 2 2 12 54.74 2.06 1.6768 2 3 5 12 55.16 2.23 1.6651 5 1 1 12 56.32 2.33 1.6336 0 5 4 6 56.52 1.18 1.6282 1 5 2 12 58.29 13.52 1.5830 2 0 8 6 59.09 23.95 1.5635 2 4 4 12 59.35 9.74 1.5571 6 0 0 6 60.29 2.82 1.5350 5 0 5 6 60.69 5.78 1.5260 4 3 1 12 61.46 1.91 1.5088 4 1 6 12 62.04 1.32 1.4960 5 2 0 12 62.06 3.02 1.4956 0 0 9 2 62.57 1.73 1.4845 4 0 7 6 62.96 2.32 1.4764 4 2 5 12 65.18 7.37 1.4313 3 2 7 12 65.80 3.25 1.4192 2 5 3 12 65.80 9.62 1.4192 5 2 3 12 65.93 1.31 1.4168 1 6 1 12 66.97 2.40 1.3973 4 3 4 12 68.76 5.38 1.3652 0 4 8 6 69.74 6.03 1.3485 4 4 0 6 69.76 2.01 1.3482 3 0 9 6 70.60 4.50 1.3341 3 4 5 12 70.96 2.64 1.3282 7 0 1 6 71.25 3.12 1.3235 2 3 8 12 72.15 1.09 1.3092 0 7 2 6 72.23 4.16 1.3079 2 2 9 12 72.71 1.71 1.3005 2 4 7 12 75.50 1.16 1.2593 6 1 5 12 76.54 2.66 1.2446 2 5 6 12 78.53 4.68 1.2180 4 2 8 12 79.23 5.02 1.2091 6 2 4 12 80.29 1.02 1.1958 0 7 5 6 81.28 2.53 1.1837 2 0 11 6 83.64 1.64 1.1562 1 2 11 12 84.67 1.48 1.1447 1 6 7 12 88.65 1.72 1.1033 0 8 4 6 89.36 1.65 1.0964 7 0 7 6 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.