LiGaS2 Leal-Gonzalez J, Melibary S S, Smith A J Acta Crystallographica C46 (1990) 2017-2019 Structure of lithium gallium sulfide, LiGaS2 _database_code_amcsd 0010203 CELL PARAMETERS: 6.5190 7.8720 6.2380 90.000 90.000 90.000 SPACE GROUP: Pna2_1 X-RAY WAVELENGTH: 1.541838 Cell Volume: 320.119 Density (g/cm3): 2.921 MAX. ABS. INTENSITY / VOLUME**2: 20.02591468 RIR: 2.232 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.66 88.39 5.0209 1 1 0 4 18.14 100.00 4.8891 0 1 1 2 22.73 24.26 3.9113 1 1 1 4 26.45 66.37 3.3695 1 2 0 4 27.36 44.56 3.2595 2 0 0 2 28.62 68.34 3.1190 0 0 2 1 29.66 10.53 3.0115 2 1 0 4 30.14 45.82 2.9646 1 2 1 4 30.95 17.33 2.8889 2 0 1 2 33.03 11.33 2.7120 2 1 1 4 33.83 22.99 2.6494 1 1 2 4 36.93 8.79 2.4342 1 3 0 4 37.17 10.94 2.4187 0 3 1 2 39.37 22.96 2.2889 1 2 2 4 39.75 7.62 2.2677 1 3 1 4 40.01 15.83 2.2535 2 0 2 2 41.69 9.43 2.1665 2 1 2 4 43.19 1.65 2.0947 3 1 0 4 44.32 5.58 2.0440 2 3 0 4 45.10 9.28 2.0104 0 1 3 2 45.69 13.87 1.9857 3 1 1 4 46.12 27.98 1.9680 0 4 0 2 46.77 3.11 1.9424 2 3 1 4 47.32 3.02 1.9211 1 1 3 4 47.37 8.66 1.9190 1 3 2 4 47.81 48.49 1.9023 3 2 0 4 51.66 48.89 1.7695 1 2 3 4 52.18 19.98 1.7530 2 0 3 2 53.56 4.72 1.7111 2 1 3 4 53.61 4.40 1.7096 2 3 2 4 54.46 10.23 1.6847 2 4 0 4 55.19 17.07 1.6644 0 4 2 2 56.46 1.70 1.6298 4 0 0 2 56.46 5.24 1.6297 0 3 3 2 56.59 5.30 1.6265 2 4 1 4 56.68 30.45 1.6241 3 2 2 4 56.97 9.49 1.6165 3 3 1 4 57.77 3.80 1.5959 4 1 0 4 58.37 1.38 1.5810 1 3 3 4 58.54 3.59 1.5768 4 0 1 2 59.82 1.69 1.5461 4 1 1 4 60.50 3.78 1.5304 1 5 0 4 60.66 4.64 1.5265 0 5 1 2 62.35 3.22 1.4893 1 1 4 4 62.68 6.98 1.4823 2 4 2 4 62.99 6.29 1.4757 3 1 3 4 63.86 3.03 1.4576 2 3 3 4 64.51 1.26 1.4444 4 0 2 2 65.72 3.57 1.4207 4 1 2 4 67.65 3.20 1.3848 2 1 4 4 67.68 2.91 1.3845 4 3 0 4 67.79 1.68 1.3824 2 5 1 4 68.27 2.87 1.3739 1 5 2 4 71.90 3.15 1.3131 1 3 4 4 72.16 12.68 1.3090 2 4 3 4 72.50 3.45 1.3038 3 3 3 4 73.36 1.74 1.2906 2 5 2 4 73.65 2.33 1.2862 1 6 0 4 73.88 7.77 1.2827 4 0 3 2 75.07 2.44 1.2654 4 3 2 4 75.47 2.47 1.2597 1 6 1 4 75.78 1.19 1.2552 4 4 0 4 75.79 1.51 1.2552 0 5 3 2 76.22 1.85 1.2491 3 5 1 4 76.89 1.32 1.2398 2 3 4 4 77.05 4.09 1.2377 5 2 0 4 77.58 2.73 1.2306 4 4 1 4 78.84 1.25 1.2140 5 2 1 4 80.83 1.97 1.1891 1 6 2 4 82.43 11.53 1.1700 1 2 5 4 82.85 4.93 1.1652 2 0 5 2 82.91 1.07 1.1645 4 4 2 4 84.15 3.48 1.1504 5 2 2 4 86.35 1.00 1.1267 0 3 5 2 86.69 6.36 1.1232 3 6 0 4 87.45 1.32 1.1154 4 1 4 4 89.62 1.77 1.0939 5 1 3 4 89.62 7.65 1.0939 1 6 3 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.