N5 Ta3 Brese N, O'Keefe M, Rauch P, DiSalvo F Acta Crystallographica C47 (1991) 2291-2294 Structure of Ta3N5 at 16 K by time-of-flight neutron diffraction _cod_database_code 1005006 _database_code_amcsd 0010266 CELL PARAMETERS: 3.8862 10.2118 10.2624 90.000 90.000 90.000 SPACE GROUP: Cmcm X-RAY WAVELENGTH: 1.541838 Cell Volume: 407.264 Density (g/cm3): 9.994 MAX. ABS. INTENSITY / VOLUME**2: 214.9572523 RIR: 7.003 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.28 9.21 5.1312 0 0 2 2 17.37 43.33 5.1059 0 2 0 2 24.51 99.13 3.6321 1 1 0 4 24.60 12.54 3.6193 0 2 2 4 26.02 9.87 3.4240 1 1 1 8 30.15 14.70 2.9646 1 1 2 8 31.48 100.00 2.8419 0 2 3 4 34.97 7.26 2.5656 0 0 4 2 35.04 66.63 2.5606 1 3 0 4 35.15 15.56 2.5529 0 4 0 2 36.07 99.75 2.4902 1 1 3 8 36.15 16.57 2.4844 1 3 1 8 36.26 4.49 2.4774 0 4 1 4 39.30 8.72 2.2925 0 2 4 4 39.32 1.39 2.2911 1 3 2 8 39.42 27.71 2.2857 0 4 2 4 43.17 1.62 2.0955 1 1 4 8 44.18 3.65 2.0499 1 3 3 8 44.27 17.15 2.0460 0 4 3 4 46.75 31.45 1.9431 2 0 0 2 47.76 10.50 1.9044 0 2 5 4 50.21 1.12 1.8172 2 0 2 4 50.24 5.36 1.8160 2 2 0 4 50.35 11.17 1.8124 1 3 4 8 51.12 2.06 1.7869 1 1 5 8 51.31 2.72 1.7805 1 5 1 8 53.53 2.96 1.7120 2 2 2 8 53.58 11.02 1.7104 0 0 6 2 53.76 23.64 1.7052 1 5 2 8 53.87 2.30 1.7020 0 6 0 2 54.66 9.10 1.6790 0 6 1 4 56.76 3.49 1.6218 0 2 6 4 57.45 35.58 1.6040 2 2 3 8 57.55 16.87 1.6015 1 3 5 8 57.67 19.19 1.5984 1 5 3 8 59.69 3.23 1.5490 2 0 4 4 59.76 6.82 1.5474 1 1 6 8 59.81 6.86 1.5462 2 4 0 4 60.56 2.30 1.5289 2 4 1 8 60.79 1.58 1.5238 0 6 3 4 62.68 3.99 1.4823 2 2 4 8 62.76 13.54 1.4804 2 4 2 8 62.89 4.22 1.4778 1 5 4 8 65.64 12.39 1.4223 1 3 6 8 65.71 1.54 1.4210 0 4 6 4 66.34 5.47 1.4091 0 2 7 4 66.34 9.43 1.4089 2 4 3 8 68.73 2.16 1.3658 1 7 0 4 69.06 6.48 1.3601 2 2 5 8 69.09 9.98 1.3595 1 1 7 8 69.26 7.47 1.3567 1 5 5 8 69.42 3.99 1.3538 1 7 1 8 71.48 14.43 1.3198 1 7 2 8 72.09 9.97 1.3101 0 6 5 4 73.72 4.13 1.2851 3 1 0 4 73.81 7.96 1.2839 2 0 6 4 74.05 1.72 1.2803 2 6 0 4 74.66 1.70 1.2713 0 4 7 4 74.72 6.92 1.2704 2 6 1 8 76.40 1.01 1.2466 3 1 2 8 76.51 2.70 1.2451 2 2 6 8 76.98 5.47 1.2387 0 8 2 4 79.10 6.40 1.2107 3 3 0 4 79.19 1.70 1.2096 1 1 8 8 79.71 10.32 1.2030 3 1 3 8 79.76 1.76 1.2024 3 3 1 8 80.02 1.36 1.1991 2 6 3 8 84.46 1.52 1.1470 2 4 6 8 84.47 1.09 1.1469 1 3 8 8 84.53 4.79 1.1462 0 4 8 4 85.03 5.38 1.1407 2 2 7 8 85.22 1.81 1.1387 1 5 7 8 85.38 3.85 1.1370 1 7 5 8 87.69 1.04 1.1129 0 2 9 4 89.51 1.98 1.0949 3 3 4 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.