Effenbergerite Lin H C, Liao F L, Wang S L Acta Crystallographica C48 (1992) 1297-1299 Structure of BaCuSi4O10 Locality: synthetic _database_code_amcsd 0018737 CELL PARAMETERS: 7.4400 7.4400 16.0970 90.000 90.000 90.000 SPACE GROUP: P4/ncc X-RAY WAVELENGTH: 1.541838 Cell Volume: 891.027 Density (g/cm3): 3.527 MAX. ABS. INTENSITY / VOLUME**2: 32.65210447 RIR: 3.014 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 10.99 38.61 8.0485 0 0 2 2 16.22 5.71 5.4633 1 0 2 8 16.85 7.55 5.2609 1 1 0 4 20.16 45.95 4.4036 1 1 2 8 22.09 7.25 4.0243 0 0 4 2 25.16 26.03 3.5396 1 0 4 8 26.39 100.00 3.3768 2 0 2 8 27.37 6.09 3.2584 2 1 1 16 27.91 71.64 3.1963 1 1 4 8 29.04 37.27 3.0749 2 1 2 16 32.78 27.51 2.7317 2 0 4 8 33.40 3.14 2.6828 0 0 6 2 34.08 37.05 2.6304 2 2 0 4 35.92 12.38 2.5003 2 2 2 8 37.64 33.02 2.3900 1 1 6 8 37.96 3.29 2.3700 3 0 2 8 38.25 6.42 2.3527 3 1 0 8 38.68 1.26 2.3280 3 1 1 16 39.92 16.89 2.2582 3 1 2 16 40.99 6.49 2.2018 2 2 4 8 41.50 1.02 2.1760 2 0 6 8 43.32 4.17 2.0885 2 1 6 16 44.25 1.97 2.0467 3 2 1 16 44.61 25.46 2.0311 3 1 4 16 45.06 5.58 2.0121 0 0 8 2 45.37 2.81 1.9988 3 2 2 16 46.77 8.21 1.9423 1 0 8 8 47.89 1.50 1.8995 3 1 5 16 48.44 6.52 1.8794 1 1 8 8 48.47 2.70 1.8783 2 2 6 8 48.97 18.95 1.8600 4 0 0 4 49.65 7.55 1.8362 3 2 4 16 50.35 3.90 1.8122 4 0 2 8 50.92 1.78 1.7932 4 1 1 16 51.65 3.31 1.7698 2 0 8 8 51.67 23.50 1.7689 3 1 6 16 53.48 2.89 1.7134 3 3 2 8 55.21 7.13 1.6636 4 2 0 8 55.84 2.66 1.6465 4 1 4 16 56.48 18.01 1.6292 4 2 2 16 57.31 11.34 1.6076 3 3 4 8 57.68 3.10 1.5982 2 2 8 8 60.19 2.14 1.5374 4 2 4 16 60.55 5.91 1.5292 3 1 8 16 60.58 2.75 1.5286 4 0 6 8 62.70 1.50 1.4817 4 3 1 16 62.91 13.36 1.4773 2 0 10 8 63.36 5.12 1.4679 3 3 6 8 63.59 2.24 1.4632 4 3 2 16 64.71 5.87 1.4406 3 2 8 16 64.95 3.19 1.4357 5 1 2 16 66.40 1.37 1.4080 5 1 3 16 67.06 1.76 1.3956 5 0 4 8 68.32 2.19 1.3730 2 2 10 8 68.39 9.97 1.3717 5 1 4 16 68.73 4.37 1.3658 4 0 8 8 68.97 5.48 1.3617 5 2 2 16 70.04 2.52 1.3434 4 1 8 16 70.16 2.09 1.3414 0 0 12 2 71.34 1.87 1.3220 3 3 8 8 71.46 1.06 1.3201 1 0 12 8 71.77 2.47 1.3152 4 4 0 4 72.87 1.54 1.2980 4 4 2 8 73.92 2.51 1.2821 4 2 8 16 73.95 6.37 1.2818 5 1 6 16 74.34 1.22 1.2759 5 3 0 8 75.43 1.76 1.2602 5 3 2 16 76.88 1.23 1.2400 6 0 0 4 77.47 1.29 1.2320 5 1 7 16 77.96 2.32 1.2255 6 0 2 8 78.67 2.72 1.2163 5 3 4 16 79.21 1.26 1.2092 6 1 2 16 80.24 2.06 1.1964 5 0 8 8 80.35 5.33 1.1950 2 2 12 8 81.48 2.37 1.1812 5 1 8 16 81.89 1.79 1.1764 6 2 0 8 82.84 1.41 1.1653 3 1 12 16 82.95 2.99 1.1640 6 2 2 16 83.58 8.39 1.1568 4 2 10 16 83.99 6.67 1.1523 5 3 6 16 86.12 2.11 1.1291 6 2 4 16 86.54 1.11 1.1247 3 2 12 16 86.68 1.46 1.1233 1 1 14 8 88.90 1.69 1.1009 4 4 8 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.