Cu O12 P3 Zr2 Bussereau I, Belkhiria M, Gravereau P, Boireau A, Soubeyroux J, Olazcuaga R, Le Flem G Acta Crystallographica C48 (1992) 1741-1744 Structure of CuZr2(PO4)3 by X-ray and neutron powder diffraction _cod_database_code 1008577 _database_code_amcsd 0016468 CELL PARAMETERS: 8.9018 8.9018 22.2021 90.000 90.000 120.000 SPACE GROUP: R-3c X-RAY WAVELENGTH: 1.541838 Cell Volume: 1523.633 Density (g/cm3): 3.471 MAX. ABS. INTENSITY / VOLUME**2: 27.88500761 RIR: 2.616 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.99 2.79 6.3321 0 1 2 6 19.71 43.66 4.5045 1 0 4 6 19.95 100.00 4.4509 1 1 0 6 23.32 73.47 3.8142 1 1 3 12 24.45 1.47 3.6413 2 0 2 6 28.19 46.50 3.1660 0 2 4 6 30.95 12.08 2.8890 2 1 1 12 31.44 61.36 2.8454 1 1 6 12 31.75 1.05 2.8183 1 2 2 12 34.34 8.83 2.6112 0 1 8 6 34.77 32.22 2.5799 2 1 4 12 34.92 23.19 2.5697 3 0 0 6 40.03 7.17 2.2522 2 0 8 6 41.87 3.85 2.1577 1 1 9 12 42.11 1.08 2.1458 2 1 7 12 42.41 2.41 2.1312 2 2 3 12 42.85 1.05 2.1107 0 3 6 6 43.08 4.67 2.0996 3 1 2 12 45.12 19.73 2.0096 1 2 8 12 45.46 19.66 1.9952 1 3 4 12 47.18 2.20 1.9264 3 1 5 12 47.24 3.90 1.9239 0 2 10 6 47.69 10.37 1.9071 2 2 6 12 47.91 7.48 1.8989 0 4 2 6 49.25 2.34 1.8502 0 0 12 2 50.10 2.72 1.8207 4 0 4 6 51.55 3.56 1.7729 1 3 7 12 51.77 17.52 1.7660 2 1 10 12 53.65 1.27 1.7084 1 1 12 12 54.15 6.65 1.6938 3 1 8 12 54.45 17.65 1.6851 3 2 4 12 54.55 14.59 1.6823 4 1 0 12 56.06 1.54 1.6404 4 1 3 12 58.29 3.01 1.5830 0 4 8 6 59.51 6.50 1.5533 0 1 14 6 60.08 12.46 1.5401 1 3 10 12 60.45 2.23 1.5314 1 4 6 12 60.45 2.11 1.5314 4 1 6 12 62.25 1.60 1.4915 2 3 8 12 62.52 6.23 1.4856 0 5 4 6 62.61 2.90 1.4836 3 3 0 6 63.37 1.09 1.4677 3 1 11 12 63.42 6.33 1.4666 2 0 14 6 63.97 6.19 1.4554 4 0 10 6 65.62 3.30 1.4227 2 2 12 12 66.33 5.92 1.4092 2 4 4 12 66.58 2.55 1.4045 1 1 15 12 67.21 5.71 1.3929 1 2 14 12 67.74 4.89 1.3833 3 2 10 12 67.82 1.37 1.3819 5 1 1 12 70.04 9.41 1.3434 5 1 4 12 71.35 1.78 1.3218 1 5 5 12 73.40 1.22 1.2900 4 2 8 12 73.74 5.49 1.2849 6 0 0 6 74.49 2.38 1.2737 3 1 14 12 74.82 2.03 1.2690 5 1 7 12 77.21 1.09 1.2356 4 3 4 12 77.29 2.89 1.2345 5 2 0 12 77.37 2.04 1.2335 0 0 18 2 78.53 2.65 1.2181 2 4 10 12 80.87 1.01 1.1887 1 1 18 12 81.53 3.55 1.1807 2 3 14 12 82.35 1.46 1.1710 2 5 6 12 82.35 1.79 1.1710 5 2 6 12 83.93 4.37 1.1529 3 4 8 12 84.18 1.90 1.1501 1 6 4 12 87.78 1.73 1.1120 0 3 18 6 87.78 1.86 1.1120 3 0 18 6 88.43 1.23 1.1055 5 0 14 6 88.92 4.44 1.1007 4 3 10 12 89.11 1.00 1.0988 0 1 20 6 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.