Cu O12 P3 Zr2 Bussereau I, Belkhiria M, Gravereau P, Boireau A, Soubeyroux J, Olazcuaga R, Le Flem G Acta Crystallographica C48 (1992) 1741-1744 Structure of CuZr2(PO4)3 by X-ray and neutron powder diffraction _cod_database_code 1008578 _database_code_amcsd 0016469 CELL PARAMETERS: 8.8920 8.8920 22.1900 90.000 90.000 120.000 SPACE GROUP: R-3c X-RAY WAVELENGTH: 1.541838 Cell Volume: 1519.452 Density (g/cm3): 3.481 MAX. ABS. INTENSITY / VOLUME**2: 26.94402344 RIR: 2.520 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.00 3.41 6.3262 0 1 2 6 19.72 42.98 4.5012 1 0 4 6 19.97 100.00 4.4460 1 1 0 6 23.34 81.42 3.8106 1 1 3 12 24.47 1.85 3.6375 2 0 2 6 28.21 46.80 3.1631 0 2 4 6 30.99 12.61 2.8859 2 1 1 12 31.46 66.36 2.8432 1 1 6 12 34.36 10.71 2.6096 0 1 8 6 34.81 32.53 2.5774 2 1 4 12 34.95 25.65 2.5669 3 0 0 6 40.06 7.93 2.2506 2 0 8 6 41.90 3.97 2.1562 1 1 9 12 42.15 1.23 2.1440 2 1 7 12 42.46 2.58 2.1289 2 2 3 12 42.89 1.41 2.1087 0 3 6 6 43.13 4.83 2.0973 3 1 2 12 45.15 19.99 2.0080 1 2 8 12 45.51 19.87 1.9932 1 3 4 12 47.23 1.77 1.9245 3 1 5 12 47.28 4.34 1.9226 0 2 10 6 47.73 11.67 1.9053 2 2 6 12 47.96 7.77 1.8968 0 4 2 6 49.28 2.03 1.8492 0 0 12 2 50.16 2.93 1.8188 4 0 4 6 51.60 3.61 1.7713 1 3 7 12 51.81 18.74 1.7647 2 1 10 12 53.68 1.23 1.7074 1 1 12 12 54.20 6.69 1.6922 3 1 8 12 54.51 18.63 1.6834 3 2 4 12 54.61 15.93 1.6804 4 1 0 12 56.13 1.45 1.6387 4 1 3 12 58.35 2.78 1.5816 0 4 8 6 59.55 6.95 1.5525 0 1 14 6 60.13 13.04 1.5388 1 3 10 12 60.52 1.99 1.5299 1 4 6 12 60.52 1.99 1.5299 4 1 6 12 62.31 1.47 1.4901 2 3 8 12 62.60 6.54 1.4840 0 5 4 6 62.69 2.78 1.4820 3 3 0 6 63.43 1.18 1.4665 3 1 11 12 63.47 6.75 1.4657 2 0 14 6 64.03 5.71 1.4542 4 0 10 6 65.68 2.94 1.4216 2 2 12 12 66.41 6.21 1.4077 2 4 4 12 66.63 2.48 1.4037 1 1 15 12 67.26 5.84 1.3920 1 2 14 12 67.80 5.09 1.3821 3 2 10 12 67.90 1.47 1.3804 5 1 1 12 70.12 9.94 1.3420 5 1 4 12 71.44 1.72 1.3204 1 5 5 12 73.48 1.26 1.2887 4 2 8 12 73.83 5.23 1.2834 6 0 0 6 74.56 2.61 1.2728 3 1 14 12 74.91 1.99 1.2677 5 1 7 12 77.31 1.20 1.2343 4 3 4 12 77.39 2.64 1.2331 5 2 0 12 77.42 2.13 1.2328 0 0 18 2 78.62 2.95 1.2169 2 4 10 12 81.60 3.62 1.1798 2 3 14 12 82.45 1.91 1.1698 5 2 6 12 82.45 1.41 1.1698 2 5 6 12 84.04 4.35 1.1517 3 4 8 12 84.29 2.13 1.1489 1 6 4 12 87.85 1.91 1.1113 3 0 18 6 87.85 1.76 1.1113 0 3 18 6 88.52 1.36 1.1046 5 0 14 6 89.03 4.94 1.0996 4 3 10 12 89.18 1.31 1.0982 0 1 20 6 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.