LiGaSi2O6 Sato A, Osawa T, Ohashi H Acta Crystallographica C50 (1994) 487-488 LiGaSi2O6 Note: anisoU's from ICSD _database_code_amcsd 0010289 CELL PARAMETERS: 9.5610 8.5690 5.2680 90.000 110.244 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 404.937 Density (g/cm3): 3.753 MAX. ABS. INTENSITY / VOLUME**2: 21.25250952 RIR: 1.844 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.29 81.42 6.1962 1 1 0 4 19.79 3.63 4.4852 2 0 0 2 20.13 43.09 4.4120 -1 1 1 4 20.73 30.46 4.2845 0 2 0 2 25.60 37.71 3.4797 1 1 1 4 30.16 100.00 2.9630 -2 2 1 4 31.69 63.57 2.8232 3 1 0 4 32.91 8.78 2.7217 1 3 0 4 35.76 6.15 2.5113 -1 1 2 4 35.96 20.07 2.4975 -1 3 1 4 36.35 33.58 2.4713 0 0 2 2 37.78 27.86 2.3814 2 2 1 4 39.44 3.40 2.2849 1 3 1 4 39.86 2.92 2.2614 -3 1 2 4 40.91 2.93 2.2060 -2 2 2 4 42.18 2.50 2.1423 0 4 0 2 42.50 20.13 2.1272 1 1 2 4 43.25 19.16 2.0919 -3 3 1 4 43.58 10.18 2.0770 -4 2 1 4 44.16 9.05 2.0511 -4 0 2 2 46.18 1.26 1.9656 0 4 1 4 47.01 2.04 1.9331 2 4 0 4 47.77 4.64 1.9039 2 0 2 2 47.91 15.35 1.8989 -2 4 1 4 48.80 8.29 1.8660 -5 1 1 4 49.25 3.52 1.8500 -4 2 2 4 50.35 3.00 1.8122 -3 3 2 4 51.90 2.04 1.7618 3 3 1 4 52.74 1.05 1.7356 -5 1 2 4 53.41 3.73 1.7156 2 4 1 4 54.07 1.48 1.6961 -1 1 3 4 54.51 8.38 1.6834 1 5 0 4 54.83 4.28 1.6744 4 2 1 4 56.66 17.65 1.6245 -2 2 3 4 56.88 9.22 1.6187 0 4 2 4 56.98 9.81 1.6162 3 1 2 4 57.98 2.39 1.5906 -4 4 1 4 58.05 17.81 1.5888 -5 3 1 4 59.69 8.27 1.5491 4 4 0 4 60.25 4.00 1.5361 -6 0 2 2 61.08 1.06 1.5172 -4 2 3 4 61.61 3.59 1.5054 1 1 3 4 61.76 2.63 1.5020 5 1 1 4 62.08 3.68 1.4951 6 0 0 2 62.22 2.60 1.4921 -6 2 1 4 62.46 5.50 1.4869 3 5 0 4 62.71 2.71 1.4815 -4 4 2 4 62.79 9.42 1.4799 -1 3 3 4 62.94 3.97 1.4767 -5 1 3 4 63.23 3.35 1.4707 -3 3 3 4 64.97 1.94 1.4353 -1 5 2 4 65.13 2.90 1.4323 4 0 2 2 65.34 6.07 1.4282 0 6 0 2 67.56 1.28 1.3866 4 4 1 4 67.72 7.99 1.3836 -3 5 2 4 69.15 2.28 1.3584 4 2 2 4 69.19 6.04 1.3578 -2 4 3 4 69.72 1.58 1.3488 -2 6 1 4 69.76 2.64 1.3481 1 3 3 4 69.90 14.34 1.3457 5 3 1 4 70.92 3.81 1.3289 2 2 3 4 71.01 3.81 1.3274 -5 3 3 4 71.03 9.60 1.3271 -7 1 2 4 72.57 1.17 1.3026 -6 2 3 4 72.84 4.51 1.2985 -3 1 4 4 73.62 4.19 1.2867 -4 0 4 2 74.93 2.85 1.2674 7 1 0 4 75.91 2.02 1.2535 6 2 1 4 76.28 1.55 1.2483 -6 4 2 4 77.14 8.49 1.2365 0 6 2 4 77.20 2.22 1.2356 0 0 4 2 79.58 1.30 1.2046 4 6 0 4 80.68 1.80 1.1909 -1 7 1 4 80.70 1.05 1.1907 4 4 2 4 81.00 6.52 1.1870 3 5 2 4 82.24 2.39 1.1722 -6 0 4 2 82.26 1.15 1.1720 -4 6 2 4 82.83 2.09 1.1654 1 7 1 4 84.88 1.22 1.1425 2 6 2 4 88.68 1.27 1.1030 -4 4 4 4 89.94 2.51 1.0908 -7 1 4 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.