NaGaSi2O6 Ohashi H, Osawa T, Sato A Acta Crystallographica C51 (1995) 2476-2477 Low-density form of NaGaSi2O6 Note: anisoU's from ICSD _database_code_amcsd 0010305 CELL PARAMETERS: 9.5573 8.7019 5.2705 90.000 107.637 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 417.726 Density (g/cm3): 3.893 MAX. ABS. INTENSITY / VOLUME**2: 22.32506390 RIR: 1.867 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.08 61.78 6.2919 1 1 0 4 19.49 8.84 4.5540 2 0 0 2 20.18 28.03 4.4000 -1 1 1 4 20.41 18.25 4.3509 0 2 0 2 24.89 11.29 3.5773 1 1 1 4 27.11 1.03 3.2886 0 2 1 4 28.37 1.56 3.1459 2 2 0 4 30.20 100.00 2.9593 -2 2 1 4 31.19 2.53 2.8677 -3 1 1 4 31.20 50.60 2.8666 3 1 0 4 32.39 1.66 2.7639 1 3 0 4 35.61 30.55 2.5214 -1 3 1 4 35.61 3.30 2.5212 -1 1 2 4 35.75 38.29 2.5114 0 0 2 2 36.75 41.13 2.4458 2 2 1 4 38.60 2.35 2.3326 1 3 1 4 39.58 2.01 2.2770 4 0 0 2 40.42 2.94 2.2318 -3 1 2 4 40.45 1.42 2.2301 3 1 1 4 41.41 19.64 2.1806 1 1 2 4 41.51 1.66 2.1755 0 4 0 2 41.52 1.45 2.1751 0 2 2 4 43.12 20.64 2.0977 -3 3 1 4 43.13 1.16 2.0973 3 3 0 4 43.63 13.87 2.0746 -4 2 1 4 44.91 10.71 2.0184 -4 0 2 2 45.43 3.53 1.9963 0 4 1 4 46.25 1.85 1.9630 2 4 0 4 46.27 6.64 1.9621 2 0 2 2 47.48 7.13 1.9151 -2 4 1 4 48.88 4.33 1.8635 -5 1 1 4 49.80 2.36 1.8310 -4 2 2 4 50.52 1.40 1.8065 -3 3 2 4 50.55 4.60 1.8056 3 3 1 4 52.20 2.59 1.7524 2 4 1 4 53.28 3.50 1.7192 4 2 1 4 53.61 12.09 1.7095 1 5 0 4 53.62 1.74 1.7093 -1 1 3 4 55.08 4.80 1.6673 3 1 2 4 55.92 7.67 1.6443 0 4 2 4 56.61 15.79 1.6258 -2 2 3 4 57.63 1.19 1.5996 -4 4 1 4 57.85 16.35 1.5939 -5 3 1 4 58.70 8.40 1.5730 4 4 0 4 59.12 1.73 1.5626 0 2 3 4 59.98 1.66 1.5422 5 1 1 4 60.09 1.45 1.5398 1 1 3 4 61.01 5.75 1.5187 -6 0 2 2 61.04 4.43 1.5180 6 0 0 2 61.40 7.21 1.5099 3 5 0 4 61.78 2.48 1.5016 -4 2 3 4 62.05 3.63 1.4958 -6 2 1 4 62.12 12.70 1.4942 -1 3 3 4 62.80 1.54 1.4797 -4 4 2 4 62.85 5.68 1.4786 4 0 2 2 63.42 2.34 1.4667 -3 3 3 4 64.01 2.08 1.4546 -5 1 3 4 64.13 1.13 1.4521 -1 5 2 4 64.22 5.09 1.4503 0 6 0 2 66.83 2.59 1.4000 4 2 2 4 67.38 11.02 1.3898 -3 5 2 4 68.00 14.36 1.3787 5 3 1 4 68.08 3.20 1.3772 1 5 2 4 68.09 1.41 1.3770 1 3 3 4 68.78 3.24 1.3649 -2 4 3 4 68.81 6.09 1.3643 2 2 3 4 71.69 7.87 1.3165 -7 1 2 4 71.78 4.49 1.3150 -5 3 3 4 73.12 6.03 1.2943 -3 1 4 4 73.61 2.47 1.2868 7 1 0 4 73.75 3.94 1.2847 6 2 1 4 74.41 1.90 1.2750 -4 0 4 2 75.73 7.50 1.2559 0 6 2 4 75.75 3.74 1.2557 0 0 4 2 76.50 1.26 1.2453 -6 4 2 4 78.13 1.10 1.2233 4 6 0 4 78.16 1.96 1.2229 4 4 2 4 78.72 7.32 1.2157 3 5 2 4 79.33 2.51 1.2078 -1 7 1 4 81.16 2.88 1.1851 1 7 1 4 83.79 3.58 1.1545 -6 0 4 2 84.32 1.95 1.1486 -8 2 1 4 85.24 1.33 1.1385 8 0 0 2 88.99 1.17 1.1000 -4 4 4 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.