Ca9Nd(PO4)5(SiO4)F1.5O.25 Boyer L, Savariault J M, Carpena J, Lacout J L Acta Crystallographica C54 (1998) 1057-1059 A neodymium-substituted britholite compound Locality: synthetic _database_code_amcsd 0010315 CELL PARAMETERS: 9.3938 9.3938 6.9013 90.000 90.000 120.000 SPACE GROUP: P6_3/m X-RAY WAVELENGTH: 1.541838 Cell Volume: 527.405 Density (g/cm3): 3.481 MAX. ABS. INTENSITY / VOLUME**2: 22.49633459 RIR: 2.104 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 10.88 1.63 8.1353 1 0 0 6 16.85 1.91 5.2627 1 0 1 12 18.89 1.66 4.6969 1 1 0 6 21.85 9.43 4.0676 2 0 0 6 25.82 32.61 3.4506 0 0 2 2 28.09 14.39 3.1767 1 0 2 12 29.04 15.46 3.0748 2 1 0 6 29.04 2.42 3.0748 1 2 0 6 31.86 32.40 2.8087 1 2 1 12 31.86 67.60 2.8087 2 1 1 12 32.19 37.83 2.7809 1 1 2 12 33.03 42.09 2.7118 3 0 0 6 34.07 12.49 2.6314 2 0 2 12 35.57 2.03 2.5239 3 0 1 12 39.24 1.43 2.2957 2 1 2 12 39.24 1.36 2.2957 1 2 2 12 39.96 12.91 2.2563 1 3 0 6 39.96 3.31 2.2563 3 1 0 6 40.58 3.01 2.2233 2 2 1 12 42.14 2.00 2.1446 1 3 1 12 42.14 1.70 2.1446 3 1 1 12 43.82 5.95 2.0659 1 1 3 12 44.55 2.59 2.0338 4 0 0 6 45.29 2.90 2.0024 2 0 3 12 46.79 23.87 1.9415 2 2 2 12 48.19 7.43 1.8884 1 3 2 12 48.19 4.10 1.8884 3 1 2 12 48.79 2.78 1.8664 2 3 0 6 49.48 22.80 1.8420 2 1 3 12 49.48 10.27 1.8420 1 2 3 12 50.67 7.36 1.8016 2 3 1 12 50.67 9.02 1.8016 3 2 1 12 51.48 7.47 1.7753 1 4 0 6 51.48 5.01 1.7753 4 1 0 6 52.21 14.99 1.7521 4 0 2 12 53.08 13.34 1.7253 0 0 4 2 56.02 3.71 1.6416 3 2 2 12 57.19 1.08 1.6108 3 1 3 12 60.19 3.68 1.5374 2 4 0 6 60.65 5.03 1.5268 3 3 1 12 61.64 1.64 1.5046 2 1 4 12 61.64 2.39 1.5046 1 2 4 12 61.82 1.45 1.5006 2 4 1 12 63.18 9.64 1.4717 5 0 2 12 63.69 1.05 1.4611 5 1 0 6 63.96 6.40 1.4557 3 0 4 12 64.27 5.45 1.4494 3 2 3 12 65.27 5.04 1.4295 5 1 1 12 65.46 1.94 1.4257 3 3 2 12 69.91 1.00 1.3455 1 5 2 12 71.74 1.10 1.3157 4 0 4 12 71.91 3.25 1.3130 4 3 1 12 72.57 1.62 1.3027 5 2 0 6 74.06 1.30 1.2801 2 5 1 12 74.06 1.60 1.2801 5 2 1 12 74.19 2.29 1.2782 2 4 3 12 75.31 1.07 1.2620 6 0 2 12 75.50 3.64 1.2592 2 1 5 12 75.50 1.86 1.2592 1 2 5 12 76.37 1.32 1.2470 3 4 2 12 76.84 1.22 1.2406 6 1 0 6 77.08 2.20 1.2373 4 1 4 12 77.08 4.35 1.2373 1 4 4 12 77.37 3.07 1.2334 5 1 3 12 78.48 4.69 1.2187 2 5 2 12 81.27 1.05 1.1837 5 0 4 12 83.63 2.90 1.1562 4 3 3 12 84.17 1.45 1.1502 0 0 6 2 84.39 1.33 1.1478 4 2 4 12 84.39 1.79 1.1478 2 4 4 12 85.70 1.18 1.1336 5 2 3 12 87.27 2.94 1.1172 1 1 6 12 87.48 1.57 1.1150 5 1 4 12 88.00 1.18 1.1098 3 2 5 12 88.00 1.44 1.1098 2 3 5 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.