Cd2As2O7 Weil M Acta Crystallographica E57 (2001) i28-i29 Cadmium(II) diarsenate(V), Cd2As2O7 _database_code_amcsd 0010354 CELL PARAMETERS: 6.9446 9.0365 4.8530 90.000 101.770 90.000 SPACE GROUP: C2/m X-RAY WAVELENGTH: 1.541838 Cell Volume: 298.146 Density (g/cm3): 5.420 MAX. ABS. INTENSITY / VOLUME**2: 86.34511386 RIR: 5.187 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 16.32 10.30 5.4327 1 1 0 4 18.68 7.84 4.7510 0 0 1 2 26.87 38.47 3.3183 1 1 1 4 27.24 100.00 3.2741 0 2 1 4 29.01 59.67 3.0775 -2 0 1 2 32.51 22.51 2.7540 1 3 0 4 32.97 42.26 2.7164 2 2 0 4 35.47 14.34 2.5310 2 0 1 2 36.33 10.62 2.4729 -1 3 1 4 37.87 8.48 2.3755 0 0 2 2 38.82 7.67 2.3197 -1 1 2 4 39.14 8.69 2.3015 1 3 1 4 39.91 6.04 2.2591 0 4 0 2 40.87 3.60 2.2081 2 2 1 4 41.06 4.48 2.1981 3 1 0 4 41.71 4.19 2.1656 -2 0 2 2 41.72 7.20 2.1649 -3 1 1 4 43.02 2.62 2.1026 0 2 2 4 44.02 1.57 2.0569 1 1 2 4 44.40 2.65 2.0402 0 4 1 4 46.50 18.02 1.9529 -2 2 2 4 48.50 1.37 1.8771 -1 3 2 4 48.98 1.50 1.8597 3 1 1 4 50.09 6.77 1.8211 -2 4 1 4 50.39 3.92 1.8109 3 3 0 4 50.96 5.48 1.7922 -3 3 1 4 51.21 5.11 1.7838 2 0 2 2 52.38 5.63 1.7466 1 5 0 4 52.94 18.41 1.7295 1 3 2 4 53.95 8.64 1.6996 4 0 0 2 54.44 1.75 1.6854 2 4 1 4 55.06 3.42 1.6679 -1 5 1 4 55.37 4.09 1.6592 2 2 2 4 56.19 1.90 1.6370 0 4 2 4 57.13 9.85 1.6122 1 5 1 4 57.33 8.00 1.6072 3 3 1 4 57.47 9.91 1.6035 -4 2 1 4 58.26 2.27 1.5837 0 0 3 2 58.87 7.35 1.5687 -3 3 2 4 59.12 2.53 1.5627 -2 0 3 2 60.13 4.69 1.5388 -4 0 2 2 61.58 4.26 1.5061 0 6 0 2 61.59 1.25 1.5059 4 0 1 2 62.11 1.45 1.4945 0 2 3 4 62.93 2.06 1.4769 -2 2 3 4 63.05 3.64 1.4745 3 1 2 4 63.85 3.64 1.4579 1 1 3 4 64.55 6.45 1.4438 -1 5 2 4 65.32 3.78 1.4286 4 2 1 4 65.47 1.91 1.4256 -3 1 3 4 65.52 9.07 1.4247 -1 3 3 4 66.13 4.38 1.4130 3 5 0 4 66.61 4.16 1.4040 -3 5 1 4 69.48 3.68 1.3528 -2 6 1 4 73.12 1.07 1.2943 2 6 1 4 74.04 2.19 1.2803 2 2 3 4 74.63 2.30 1.2718 -4 4 2 4 74.87 1.11 1.2683 1 7 0 4 76.32 2.69 1.2477 -4 2 3 4 76.93 3.33 1.2393 5 3 0 4 77.09 1.97 1.2371 -1 7 1 4 77.60 2.49 1.2304 5 1 1 4 79.79 1.85 1.2019 -1 1 4 4 79.94 1.07 1.2001 -2 0 4 2 83.59 1.83 1.1567 -6 0 1 2 84.03 4.12 1.1517 3 5 2 4 84.31 1.88 1.1487 0 2 4 4 84.76 4.12 1.1438 1 5 3 4 86.23 3.05 1.1280 -3 5 3 4 86.30 1.56 1.1272 4 6 0 4 88.37 2.75 1.1061 3 3 3 4 88.83 2.15 1.1015 1 7 2 4 89.08 1.53 1.0991 6 2 0 4 89.10 2.79 1.0989 0 8 1 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.