Cd3[Si3O9] Weil M Acta Crystallographica E61 (2005) i102-i104 Parawollastonite-type Cd3[Si3O9] _database_code_amcsd 0010446 CELL PARAMETERS: 6.9463 7.2563 15.0697 90.000 94.791 90.000 SPACE GROUP: P2_1/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 756.926 Density (g/cm3): 4.962 MAX. ABS. INTENSITY / VOLUME**2: 62.99079123 RIR: 4.134 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 11.79 6.43 7.5085 0 0 2 2 12.79 12.67 6.9220 1 0 0 2 16.68 3.43 5.3154 -1 0 2 2 18.14 49.03 4.8899 1 0 2 2 23.70 8.49 3.7543 0 0 4 2 24.37 1.30 3.6527 -1 1 3 4 25.74 13.50 3.4610 2 0 0 2 26.04 15.53 3.4221 -1 0 4 2 26.74 1.86 3.3344 0 1 4 4 27.46 22.35 3.2480 -2 0 2 2 28.17 17.61 3.1676 -1 2 1 4 28.63 1.22 3.1177 1 2 1 4 28.75 2.05 3.1054 -2 1 1 4 29.30 21.99 3.0479 2 0 2 2 30.15 2.21 2.9646 -2 1 2 4 30.43 100.00 2.9377 0 2 3 4 32.26 1.06 2.7751 0 1 5 4 32.52 12.32 2.7532 -1 2 3 4 33.72 16.53 2.6577 -2 0 4 2 35.88 15.10 2.5028 0 0 6 2 36.00 15.56 2.4948 -2 2 1 4 36.74 21.86 2.4463 2 2 1 4 36.76 11.57 2.4449 2 0 4 2 37.16 3.81 2.4192 -1 0 6 2 38.93 8.07 2.3136 0 2 5 4 39.04 2.71 2.3073 3 0 0 2 39.24 3.95 2.2959 -2 2 3 4 39.90 18.26 2.2592 -3 0 2 2 40.30 3.05 2.2380 -1 2 5 4 41.27 3.75 2.1874 2 2 3 4 41.96 29.71 2.1530 1 2 5 4 42.78 1.74 2.1137 -2 0 6 2 45.75 3.81 1.9833 -2 2 5 4 46.52 2.17 1.9522 2 0 6 2 47.51 9.23 1.9137 3 2 1 4 47.97 1.23 1.8964 3 0 4 2 48.50 2.69 1.8771 0 0 8 2 48.73 2.55 1.8687 2 2 5 4 49.35 3.46 1.8466 0 2 7 4 50.21 5.09 1.8171 -1 2 7 4 50.30 15.59 1.8141 0 4 0 2 51.50 4.77 1.7746 1 0 8 2 51.55 5.32 1.7728 3 2 3 4 52.12 1.32 1.7548 1 4 0 4 52.91 9.85 1.7305 4 0 0 2 53.91 7.21 1.7008 1 4 2 4 54.32 14.45 1.6890 -3 2 5 4 54.62 12.79 1.6802 -2 2 7 4 56.45 2.12 1.6300 3 0 6 2 57.34 2.07 1.6067 2 4 0 4 57.50 2.56 1.6028 -1 4 4 4 58.26 4.94 1.5838 -2 4 2 4 58.30 10.06 1.5827 2 2 7 4 59.28 3.42 1.5589 2 4 2 4 60.77 6.48 1.5241 -4 2 3 4 60.97 1.98 1.5196 -3 0 8 2 61.13 3.29 1.5159 0 2 9 4 61.63 5.38 1.5049 -1 2 9 4 61.78 1.22 1.5017 0 0 10 2 61.93 5.41 1.4983 -2 4 4 4 62.08 1.27 1.4951 -3 2 7 4 62.67 2.45 1.4825 -4 0 6 2 63.32 4.84 1.4688 0 4 6 4 63.74 10.14 1.4601 4 2 3 4 63.90 4.29 1.4569 2 4 4 4 64.17 1.85 1.4514 -1 4 6 4 64.60 1.34 1.4428 1 0 10 2 65.68 4.19 1.4217 -2 0 10 2 66.05 5.68 1.4145 -3 4 2 4 68.44 2.77 1.3709 4 0 6 2 69.95 1.48 1.3449 4 2 5 4 70.40 3.97 1.3374 2 0 10 2 70.51 1.10 1.3356 -5 0 4 2 72.06 1.22 1.3106 -4 2 7 4 72.91 1.08 1.2974 -5 2 1 4 74.29 1.25 1.2767 -5 2 3 4 74.85 3.41 1.2686 1 4 8 4 76.00 5.48 1.2522 4 4 0 4 76.17 2.17 1.2499 -1 0 12 2 76.93 2.15 1.2393 1 2 11 4 78.00 1.43 1.2250 3 2 9 4 78.96 1.13 1.2124 3 4 6 4 80.84 1.07 1.1890 -1 6 1 4 81.11 2.42 1.1858 -4 2 9 4 81.96 3.07 1.1756 0 6 3 4 82.87 1.93 1.1649 -3 4 8 4 83.68 1.72 1.1557 5 2 5 4 84.38 1.35 1.1479 -4 4 6 4 85.47 1.73 1.1360 2 6 1 4 86.08 1.07 1.1296 -6 0 4 2 86.11 1.15 1.1292 1 4 10 4 87.09 3.29 1.1190 -2 4 10 4 88.79 3.29 1.1020 1 6 5 4 89.02 1.41 1.0997 4 2 9 4 89.64 2.46 1.0937 4 4 6 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.