LaAlO3
      Nakatsuka A, Ohtaka O, Arima H, Nakayama N, Mizota T
      Acta Crystallographica E61 (2005) i148-i150
      Cubic phase of single-crystal LaAlO3 perovskite synthesized at
      4.5 GPa and 1273 K
      Locality: synthetic
      _database_code_amcsd 0010454

      CELL PARAMETERS:    3.7913   3.7913   3.7913   90.000   90.000   90.000
      SPACE GROUP: Pm-3m     
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:     54.496
      Density (g/cm3):      6.516
      MAX. ABS. INTENSITY / VOLUME**2:      209.6150993    
      RIR:     10.474
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                23.46         46.06        3.7913    1   0   0         6
                33.42        100.00        2.6809    1   1   0        12
                41.24         40.96        2.1889    1   1   1         8
                47.99         34.59        1.8957    2   0   0         6
                54.09         20.26        1.6955    2   1   0        24
                59.75         37.14        1.5478    2   1   1        24
                70.22         19.12        1.3404    2   2   0        12
                75.18          7.85        1.2638    2   2   1        24
                75.18          1.96        1.2638    3   0   0         6
                80.03         15.92        1.1989    3   1   0        24
                84.82         11.40        1.1431    3   1   1        24
                89.56          6.39        1.0945    2   2   2         8
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs
  For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.