K2FeSn(PO4)3 Zatovsky I V, Yatskin M M, Baumer V N, Slobodyanik N S, Shishkin O V Acta Crystallographica E63 (2007) i199-i199 Langbeinite-related K2FeSn(PO4)3 from single-crystal data Locality: synthetic _database_code_amcsd 0010480 CELL PARAMETERS: 9.9147 9.9147 9.9147 90.000 90.000 90.000 SPACE GROUP: P2_13 X-RAY WAVELENGTH: 1.541838 Cell Volume: 974.637 Density (g/cm3): 3.664 MAX. ABS. INTENSITY / VOLUME**2: 37.05992592 RIR: 3.294 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 15.48 27.95 5.7243 1 1 1 4 20.03 39.73 4.4340 2 0 1 12 20.03 4.41 4.4340 2 1 0 12 21.96 21.92 4.0477 2 1 1 12 26.98 7.57 3.3049 2 2 1 12 28.47 53.33 3.1353 3 0 1 12 28.47 46.67 3.1353 3 1 0 12 29.89 24.96 2.9894 3 1 1 12 32.56 3.60 2.7499 3 0 2 12 32.56 8.81 2.7499 3 2 0 12 33.83 47.75 2.6498 3 2 1 12 33.83 26.22 2.6498 3 1 2 12 37.40 3.30 2.4047 3 2 2 12 39.62 2.91 2.2746 3 3 1 12 40.70 1.05 2.2170 4 2 0 12 41.75 3.25 2.1636 4 1 2 12 42.78 1.86 2.1138 3 3 2 12 44.78 18.31 2.0238 4 2 2 12 45.76 5.59 1.9829 4 3 0 12 46.72 8.02 1.9444 4 1 3 12 46.72 2.09 1.9444 5 1 0 12 46.72 5.01 1.9444 4 3 1 12 47.66 4.35 1.9081 3 3 3 4 47.66 1.96 1.9081 5 1 1 12 49.51 7.35 1.8411 5 0 2 12 49.51 1.32 1.8411 5 2 0 12 49.51 10.05 1.8411 4 3 2 12 50.41 3.16 1.8102 5 1 2 12 52.19 2.26 1.7527 4 4 0 12 53.06 1.17 1.7259 5 2 2 12 53.06 9.66 1.7259 4 4 1 12 53.92 3.05 1.7004 5 0 3 12 53.92 1.06 1.7004 5 3 0 12 54.77 1.17 1.6759 5 3 1 12 56.45 2.56 1.6300 6 0 1 12 56.45 2.98 1.6300 6 1 0 12 57.28 7.30 1.6084 5 3 2 12 57.28 6.50 1.6084 6 1 1 12 57.28 7.08 1.6084 5 2 3 12 58.91 1.74 1.5677 6 0 2 12 58.91 1.42 1.5677 6 2 0 12 59.72 3.39 1.5484 6 2 1 12 59.72 2.06 1.5484 6 1 2 12 60.52 1.83 1.5299 5 4 1 12 60.52 5.22 1.5299 5 1 4 12 62.10 2.60 1.4947 6 2 2 12 62.88 2.90 1.4780 6 0 3 12 62.88 2.01 1.4780 5 2 4 12 62.88 4.63 1.4780 5 4 2 12 63.65 8.23 1.4618 6 3 1 12 65.19 2.21 1.4311 4 4 4 4 65.95 2.31 1.4164 6 2 3 12 65.95 2.27 1.4164 6 3 2 12 66.71 1.31 1.4022 7 0 1 12 66.71 1.33 1.4022 5 4 3 12 66.71 2.61 1.4022 5 3 4 12 67.46 1.51 1.3883 5 5 1 12 68.95 1.92 1.3619 6 1 4 12 68.95 1.72 1.3619 7 0 2 12 71.16 1.91 1.3249 6 4 2 12 71.89 1.55 1.3132 7 2 2 12 72.62 2.17 1.3019 7 0 3 12 73.35 4.08 1.2908 7 3 1 12 75.50 2.49 1.2592 6 1 5 12 77.64 1.10 1.2298 6 2 5 12 77.64 1.53 1.2298 7 4 0 12 78.35 1.39 1.2204 7 4 1 12 79.06 1.79 1.2113 7 3 3 12 80.46 1.07 1.1936 7 4 2 12 82.57 3.48 1.1685 8 2 2 12 82.57 1.20 1.1685 6 6 0 12 83.96 1.41 1.1526 8 3 1 12 83.96 2.24 1.1526 7 3 4 12 84.66 1.43 1.1449 5 5 5 4 86.05 1.33 1.1299 6 5 4 12 86.74 1.40 1.1226 7 2 5 12 86.74 2.31 1.1226 7 5 2 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.