CdCu(OH)3(NO3) Effenberger H Zeitschrift fur Kristallographie 19 (2002) 85-85 CdCu(OH)3(NO3), a new layer compound Locality: synthetic _database_code_amcsd 0019131 CELL PARAMETERS: 5.8460 6.6130 6.6970 90.000 99.440 90.000 SPACE GROUP: P2_1/m X-RAY WAVELENGTH: 1.541838 Cell Volume: 255.397 Density (g/cm3): 3.757 MAX. ABS. INTENSITY / VOLUME**2: 70.14622547 RIR: 6.079 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.40 100.00 6.6063 0 0 1 2 15.36 4.74 5.7668 1 0 0 2 18.99 7.34 4.6737 0 1 1 4 20.43 1.36 4.3463 1 1 0 4 22.06 1.30 4.0294 1 0 1 2 23.06 16.23 3.8565 -1 1 1 4 26.97 5.71 3.3065 0 2 0 2 26.99 13.16 3.3032 0 0 2 2 30.25 15.52 2.9550 0 1 2 4 31.01 9.89 2.8834 2 0 0 2 31.18 29.24 2.8685 1 2 0 4 31.76 10.09 2.8175 -2 0 1 2 31.94 5.61 2.8020 -1 1 2 4 33.01 6.32 2.7132 -1 2 1 4 34.60 5.61 2.5921 -2 1 1 4 35.11 31.96 2.5561 1 2 1 4 35.97 4.84 2.4968 2 0 1 2 36.13 4.49 2.4860 1 1 2 4 37.90 7.32 2.3736 -2 0 2 2 38.54 3.49 2.3358 2 1 1 4 39.91 4.00 2.2590 -1 2 2 4 40.37 5.90 2.2341 -2 1 2 4 41.56 1.75 2.1732 2 2 0 4 43.27 1.23 2.0910 0 3 1 4 43.31 4.84 2.0893 0 1 3 4 43.44 11.00 2.0833 1 2 2 4 43.73 5.13 2.0702 -1 1 3 4 45.00 3.31 2.0147 2 0 2 2 45.36 1.55 1.9993 -1 3 1 4 47.16 1.65 1.9272 2 1 2 4 48.60 3.28 1.8732 1 1 3 4 49.11 2.79 1.8551 -3 1 1 4 49.73 3.49 1.8335 0 3 2 4 49.75 1.91 1.8328 0 2 3 4 49.75 3.47 1.8328 -2 1 3 4 50.86 1.64 1.7952 -1 3 2 4 52.72 1.09 1.7361 -2 3 1 4 52.87 1.25 1.7317 -3 1 2 4 53.83 1.16 1.7031 1 3 2 4 54.57 1.74 1.6817 1 2 3 4 55.04 5.46 1.6686 -3 2 1 4 55.28 6.47 1.6618 3 2 0 4 55.59 5.23 1.6532 0 4 0 2 55.63 2.07 1.6523 -2 2 3 4 57.02 1.34 1.6152 -2 3 2 4 57.46 3.99 1.6038 0 4 1 4 57.52 1.38 1.6024 0 1 4 4 58.44 1.32 1.5791 2 1 3 4 58.53 1.77 1.5770 -3 2 2 4 59.23 3.02 1.5601 3 2 1 4 59.32 1.74 1.5579 0 3 3 4 59.65 1.72 1.5500 -1 3 3 4 60.12 1.54 1.5390 -3 1 3 4 60.82 1.03 1.5230 1 0 4 2 61.26 1.40 1.5131 3 1 2 4 62.59 1.26 1.4842 1 1 4 4 62.86 1.46 1.4784 0 4 2 4 63.65 1.08 1.4619 1 3 3 4 64.61 1.29 1.4424 -2 3 3 4 64.65 1.81 1.4417 4 0 0 2 65.03 1.85 1.4342 2 4 0 4 65.46 1.91 1.4259 -2 4 1 4 66.47 1.51 1.4066 3 2 2 4 66.77 2.19 1.4010 -2 2 4 4 68.01 1.38 1.3785 2 4 1 4 68.90 1.12 1.3628 4 0 1 2 69.26 1.40 1.3566 -2 4 2 4 70.45 1.21 1.3365 -1 0 5 2 80.23 1.75 1.1965 -2 2 5 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.