Ca N2 Dehlinger U Zeitschrift fur Kristallographie 65 (1927) 286-290 Ueber die Rumgruppe von (C N2 H2)2 und die Kristallstruktur von Ca C N2. _cod_database_code 1010503 _database_code_amcsd 0017418 CELL PARAMETERS: 5.1100 5.1100 5.1100 43.830 43.830 43.830 SPACE GROUP: R-3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 58.102 Density (g/cm3): 2.289 MAX. ABS. INTENSITY / VOLUME**2: 18.13140189 RIR: 2.579 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 19.25 100.00 4.6111 1 1 1 2 27.77 4.30 3.2130 1 0 0 6 29.98 86.29 2.9809 1 1 0 6 37.66 10.50 2.3887 2 1 1 6 39.07 15.91 2.3055 2 2 2 2 42.63 23.97 2.1210 2 2 1 6 47.68 43.88 1.9072 0 -1 1 6 51.88 28.29 1.7624 2 1 0 12 57.35 9.10 1.6065 2 0 0 6 62.30 1.96 1.4904 2 2 0 6 77.72 5.70 1.2287 2 -1 1 12 88.87 4.25 1.1011 1 -2 1 6 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.