Enstatite Warren B, Modell D Zeitschrift fur Kristallographie 75 (1930) 1-14 The structure of enstatite, MgSiO3 _database_code_amcsd 0018104 CELL PARAMETERS: 18.2000 8.8600 5.2000 90.000 90.000 90.000 SPACE GROUP: Pbca X-RAY WAVELENGTH: 1.541838 Cell Volume: 838.510 Density (g/cm3): 3.480 MAX. ABS. INTENSITY / VOLUME**2: 6.966123971 RIR: 0.652 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 9.72 2.74 9.1000 2 0 0 2 13.95 1.37 6.3481 2 1 0 4 19.51 3.71 4.5500 4 0 0 2 20.04 5.91 4.4300 0 2 0 2 22.10 1.93 4.0227 2 1 1 8 26.89 10.04 3.3158 1 2 1 8 27.93 23.27 3.1940 4 1 1 8 28.11 24.44 3.1741 4 2 0 4 28.22 100.00 3.1621 2 2 1 8 29.45 1.64 3.0333 6 0 0 2 30.32 83.76 2.9474 3 2 1 8 31.17 88.55 2.8698 6 1 0 4 31.66 26.72 2.8262 5 1 1 8 33.06 64.27 2.7092 4 2 1 8 34.86 4.74 2.5739 1 0 2 4 35.30 32.27 2.5429 1 3 1 8 35.74 15.00 2.5126 6 1 1 8 35.92 41.06 2.5000 2 0 2 4 36.32 30.17 2.4738 5 2 1 8 36.35 31.25 2.4715 2 3 1 8 37.64 16.59 2.3898 3 0 2 4 38.05 1.92 2.3649 3 3 1 8 39.04 3.22 2.3073 3 1 2 8 40.09 10.38 2.2493 7 1 1 8 40.33 6.69 2.2364 4 3 1 8 41.27 3.44 2.1875 4 1 2 8 41.47 5.42 2.1772 2 2 2 8 42.73 16.11 2.1160 6 3 0 4 42.74 34.39 2.1157 5 0 2 4 43.00 1.27 2.1033 3 2 2 8 43.11 9.94 2.0984 5 3 1 8 43.98 7.22 2.0590 7 2 1 8 44.00 7.63 2.0578 5 1 2 8 44.66 3.54 2.0289 8 1 1 8 44.75 7.28 2.0252 1 4 1 8 45.55 4.00 1.9915 4 4 0 4 45.62 6.90 1.9886 2 4 1 8 46.32 14.68 1.9600 6 3 1 8 46.82 9.95 1.9404 1 3 2 8 47.04 3.27 1.9318 3 4 1 8 48.26 14.12 1.8859 8 2 1 8 49.58 8.58 1.8385 7 0 2 4 49.91 2.10 1.8271 7 3 1 8 50.62 4.46 1.8031 6 2 2 8 50.71 1.99 1.8001 7 1 2 8 50.91 3.26 1.7935 4 3 2 8 51.24 4.70 1.7828 10 1 0 4 52.62 16.89 1.7393 2 5 0 4 52.78 7.22 1.7343 9 2 1 8 53.26 2.82 1.7199 5 3 2 8 53.84 9.43 1.7029 8 3 1 8 54.00 1.79 1.6981 7 2 2 8 54.59 3.56 1.6810 8 1 2 8 54.67 1.53 1.6789 1 4 2 8 54.91 3.25 1.6721 2 1 3 8 55.42 15.25 1.6579 2 4 2 8 55.73 1.34 1.6495 2 5 1 8 56.16 4.30 1.6379 3 1 3 8 56.66 3.00 1.6245 3 4 2 8 56.96 1.66 1.6166 3 5 1 8 57.06 18.09 1.6142 0 2 3 4 57.30 12.07 1.6079 1 2 3 8 57.76 17.66 1.5962 9 0 2 4 58.06 8.86 1.5888 9 3 1 8 58.12 1.29 1.5870 8 4 0 4 58.66 1.67 1.5738 4 5 1 8 58.78 1.95 1.5710 9 1 2 8 59.20 2.38 1.5608 7 3 2 8 59.68 5.07 1.5494 10 3 0 4 60.51 10.13 1.5301 6 5 0 4 61.10 16.82 1.5167 12 0 0 2 61.77 1.66 1.5017 9 2 2 8 62.27 1.53 1.4910 10 0 2 4 62.32 17.17 1.4899 1 3 3 8 62.55 16.87 1.4849 10 3 1 8 62.73 2.58 1.4812 8 3 2 8 62.94 8.67 1.4767 0 6 0 2 62.99 1.96 1.4756 5 2 3 8 63.02 7.85 1.4751 2 3 3 8 65.59 16.36 1.4234 3 5 2 8 65.74 3.24 1.4205 0 6 1 4 65.96 6.17 1.4162 1 6 1 8 66.12 2.26 1.4131 10 2 2 8 66.64 2.23 1.4035 2 6 1 8 67.05 3.19 1.3959 11 0 2 4 67.16 4.30 1.3939 4 5 2 8 67.32 20.64 1.3909 11 3 1 8 67.77 1.88 1.3828 5 3 3 8 67.99 3.49 1.3789 11 1 2 8 68.41 3.06 1.3714 7 2 3 8 68.77 1.79 1.3651 0 4 3 4 69.15 2.09 1.3585 5 5 2 8 70.19 5.37 1.3409 6 3 3 8 72.36 3.29 1.3059 12 3 1 8 72.96 4.14 1.2967 1 0 4 4 73.00 7.24 1.2960 12 1 2 8 73.01 3.66 1.2960 7 3 3 8 73.65 1.35 1.2862 14 1 0 4 73.86 3.26 1.2830 1 1 4 8 74.35 3.14 1.2758 7 5 2 8 74.50 2.05 1.2736 2 1 4 8 74.65 11.35 1.2714 2 6 2 8 75.30 1.52 1.2620 11 3 2 8 75.71 3.64 1.2562 3 6 2 8 76.16 7.87 1.2500 4 0 4 4 76.68 1.64 1.2428 10 1 3 8 77.11 1.50 1.2369 10 4 2 8 77.53 6.32 1.2313 8 5 2 8 78.92 2.21 1.2130 14 2 1 8 78.94 1.38 1.2127 5 1 4 8 79.09 1.04 1.2109 5 6 2 8 81.09 5.46 1.1860 9 5 2 8 81.58 1.62 1.1800 5 2 4 8 81.60 1.06 1.1798 2 3 4 8 83.93 1.59 1.1529 7 1 4 8 84.95 1.46 1.1417 15 2 1 8 86.16 3.84 1.1287 8 0 4 4 88.06 1.13 1.1092 11 3 3 8 88.45 3.55 1.1053 12 2 3 8 88.45 1.16 1.1053 3 6 3 8 89.35 3.08 1.0965 11 5 2 8 89.89 2.08 1.0913 4 6 3 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.