Fersilicite Wever F, Moeller H Zeitschrift fur Kristallographie 75 (1930) 362-365 Ueber den Kristallbau des Eisensilizides FeSi _cod_database_code 1011343 _database_code_amcsd 0018180 CELL PARAMETERS: 4.4670 4.4670 4.4670 90.000 90.000 90.000 SPACE GROUP: P2_13 X-RAY WAVELENGTH: 1.541838 Cell Volume: 89.135 Density (g/cm3): 6.253 MAX. ABS. INTENSITY / VOLUME**2: 114.5732760 RIR: 5.966 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 28.25 20.82 3.1586 1 1 0 12 34.79 17.62 2.5790 1 1 1 4 40.38 4.46 2.2335 2 0 0 6 45.40 11.78 1.9977 2 0 1 12 45.40 88.22 1.9977 2 1 0 12 50.01 51.04 1.8236 2 1 1 12 62.36 2.52 1.4890 2 2 1 12 66.15 1.98 1.4126 3 1 0 12 69.83 10.35 1.3469 3 1 1 12 73.43 2.68 1.2895 2 2 2 4 76.96 5.06 1.2389 3 0 2 12 76.96 1.14 1.2389 3 2 0 12 80.44 19.54 1.1939 3 1 2 12 80.44 3.87 1.1939 3 2 1 12 87.31 6.99 1.1168 4 0 0 6 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.