Hambergite Zachariasen W Zeitschrift fur Kristallographie 76 (1931) 289-302 The crystalline structure of hambergite Be2BO3(OH) _cod_database_code 1011268 _database_code_amcsd 0018127 CELL PARAMETERS: 9.7500 12.2040 4.4290 90.000 90.000 90.000 SPACE GROUP: Pbca X-RAY WAVELENGTH: 1.541838 Cell Volume: 527.002 Density (g/cm3): 2.340 MAX. ABS. INTENSITY / VOLUME**2: 4.291193265 RIR: 0.597 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 19.61 17.14 4.5272 2 1 0 4 23.23 20.51 3.8289 1 1 1 8 23.36 79.42 3.8087 2 2 0 4 24.84 13.88 3.5844 0 2 1 4 28.19 5.17 3.1659 2 1 1 8 28.58 100.00 3.1234 2 3 0 4 29.27 12.11 3.0510 0 4 0 2 30.97 3.59 2.8878 2 2 1 8 31.23 3.84 2.8639 1 3 1 8 34.68 8.35 2.5863 2 4 0 4 35.03 11.79 2.5619 3 1 1 8 35.16 2.87 2.5525 2 3 1 8 36.95 3.44 2.4331 1 4 1 8 37.35 10.32 2.4076 3 2 1 8 37.63 17.88 2.3903 4 1 0 4 40.39 46.29 2.2334 2 4 1 8 40.75 6.49 2.2145 0 0 2 2 41.37 4.86 2.1825 2 5 0 4 41.83 31.47 2.1595 1 0 2 4 42.51 9.46 2.1265 1 1 2 8 43.00 20.69 2.1035 4 1 1 8 43.27 1.31 2.0909 4 3 0 4 44.50 1.23 2.0358 1 2 2 8 44.55 1.11 2.0340 0 6 0 2 44.97 18.22 2.0156 4 2 1 8 46.38 35.37 1.9577 2 5 1 8 47.68 1.28 1.9074 1 3 2 8 47.76 4.12 1.9044 4 4 0 4 48.50 1.28 1.8772 2 6 0 4 49.30 6.17 1.8484 0 6 1 4 50.42 10.24 1.8098 3 1 2 8 50.52 2.04 1.8065 2 3 2 8 52.18 2.03 1.7529 3 2 2 8 52.29 1.88 1.7495 4 4 1 8 53.10 7.62 1.7247 4 5 0 4 54.56 1.10 1.6821 2 4 2 8 55.02 6.73 1.6689 3 3 2 8 56.02 3.87 1.6416 2 7 0 4 56.66 5.47 1.6245 4 1 2 8 58.81 1.97 1.5703 6 2 0 4 58.84 1.35 1.5694 3 4 2 8 59.16 1.65 1.5617 4 6 0 4 60.06 9.46 1.5405 5 4 1 8 60.71 4.21 1.5255 0 8 0 2 61.23 4.85 1.5138 6 1 1 8 62.78 1.00 1.4800 6 2 1 8 63.54 5.98 1.4642 3 5 2 8 64.62 2.72 1.4423 0 8 1 4 64.70 1.35 1.4406 5 5 1 8 65.03 1.14 1.4343 6 4 0 4 65.15 1.13 1.4319 2 6 2 8 66.63 1.33 1.4036 2 1 3 8 68.26 2.29 1.3739 1 3 3 8 68.80 3.43 1.3645 6 4 1 8 69.02 1.36 1.3607 4 5 2 8 71.67 3.07 1.3168 1 4 3 8 71.93 1.52 1.3127 3 2 3 8 73.19 1.73 1.2931 4 8 0 4 74.32 1.07 1.2763 3 3 3 8 74.78 3.51 1.2696 6 6 0 4 75.28 1.58 1.2623 3 7 2 8 75.94 2.93 1.2530 2 9 1 8 75.96 6.30 1.2528 1 5 3 8 76.45 1.46 1.2460 1 8 2 8 77.13 1.90 1.2366 4 2 3 8 77.62 2.34 1.2301 3 4 3 8 80.86 2.12 1.1887 6 7 0 4 81.09 1.01 1.1859 1 6 3 8 81.17 1.48 1.1850 4 9 0 4 81.26 1.01 1.1839 2 10 0 4 82.29 4.27 1.1716 5 1 3 8 82.46 1.18 1.1697 8 1 1 8 83.68 1.40 1.1557 5 2 3 8 84.76 1.70 1.1437 2 10 1 8 86.14 2.97 1.1289 8 3 1 8 86.91 1.52 1.1209 5 7 2 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.