Li2 O4 S Albright J Zeitschrift fur Kristallographie 84 (1932) 150-158 The Crystal Structure of Lithium Sulphate _cod_database_code 1010467 _database_code_amcsd 0017384 CELL PARAMETERS: 8.2500 4.9500 8.4400 90.000 107.900 90.000 SPACE GROUP: P2_1/a X-RAY WAVELENGTH: 1.541838 Cell Volume: 327.985 Density (g/cm3): 2.226 MAX. ABS. INTENSITY / VOLUME**2: 9.378084207 RIR: 1.372 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 21.08 8.32 4.2139 0 1 1 4 21.22 19.28 4.1872 1 1 0 4 21.94 19.75 4.0520 -2 0 1 2 22.14 81.76 4.0157 0 0 2 2 22.28 100.00 3.9907 -1 1 1 4 22.65 45.01 3.9253 2 0 0 2 25.55 15.41 3.4860 1 1 1 4 26.43 5.74 3.3726 -2 0 2 2 28.16 19.81 3.1694 -1 1 2 4 28.21 27.08 3.1638 2 0 1 2 28.47 5.12 3.1355 -2 1 1 4 29.03 9.58 3.0756 2 1 0 4 32.11 9.42 2.7872 -2 1 2 4 33.35 8.35 2.6866 1 1 2 4 33.62 5.06 2.6658 2 1 1 4 34.25 10.13 2.6177 -2 0 3 2 36.30 29.31 2.4750 0 2 0 2 37.41 12.05 2.4036 -3 1 1 4 38.22 10.27 2.3548 0 1 3 4 38.92 7.00 2.3141 -2 1 3 4 41.04 1.19 2.1994 2 1 2 4 42.92 4.92 2.1070 0 2 2 4 42.98 1.02 2.1044 1 1 3 4 43.21 3.46 2.0936 2 2 0 4 44.00 2.05 2.0580 -4 0 1 2 44.73 2.63 2.0260 -4 0 2 2 45.16 2.32 2.0079 0 0 4 2 46.26 1.39 1.9627 4 0 0 2 46.39 2.27 1.9575 1 2 2 4 46.57 6.70 1.9502 2 0 3 2 46.59 2.32 1.9494 2 2 1 4 46.86 4.40 1.9386 -1 1 4 4 47.76 1.21 1.9043 -2 1 4 4 47.87 1.31 1.9003 -4 1 1 4 48.35 6.16 1.8827 -4 0 3 2 48.55 3.16 1.8750 -4 1 2 4 49.99 3.62 1.8245 4 1 0 4 50.28 2.40 1.8145 2 1 3 4 50.77 1.25 1.7984 -2 2 3 4 51.20 3.56 1.7843 4 0 1 2 53.77 2.41 1.7048 1 1 4 4 54.69 3.30 1.6784 -2 0 5 2 57.50 3.78 1.6027 -1 3 1 4 58.22 1.18 1.5847 -2 2 4 4 58.91 1.50 1.5677 -4 2 2 4 59.06 1.90 1.5641 1 3 1 4 60.43 1.41 1.5318 2 2 3 4 60.61 1.04 1.5279 0 1 5 4 60.90 1.98 1.5211 2 3 0 4 61.93 1.06 1.4984 -4 2 3 4 62.01 2.05 1.4966 5 1 0 4 62.45 3.33 1.4871 -4 0 5 2 62.68 2.66 1.4821 -2 3 2 4 63.60 1.53 1.4630 2 3 1 4 65.57 2.06 1.4237 1 1 5 4 66.03 1.86 1.4149 -5 1 4 4 66.57 4.30 1.4046 0 3 3 4 66.86 1.64 1.3993 5 1 1 4 67.05 3.53 1.3959 -2 3 3 4 67.26 2.24 1.3920 4 0 3 2 68.22 1.15 1.3747 -6 0 2 2 70.33 3.94 1.3386 0 0 6 2 72.20 1.74 1.3084 6 0 0 2 72.64 1.02 1.3016 -5 1 5 4 73.20 1.91 1.2930 -6 0 4 2 73.58 1.25 1.2873 -4 3 1 4 73.75 2.14 1.2846 5 1 2 4 74.11 2.00 1.2794 -4 3 2 4 75.24 2.51 1.2630 4 3 0 4 75.47 2.03 1.2597 2 3 3 4 81.16 1.18 1.1851 -5 1 6 4 81.80 1.90 1.1774 0 2 6 4 81.87 1.07 1.1766 -2 3 5 4 83.82 1.70 1.1541 1 4 2 4 84.67 1.07 1.1447 6 0 2 2 86.18 1.11 1.1285 -3 4 1 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.