Bischofite Andress K, Gundermann J Zeitschrift fur Kristallographie 87 (1934) 345-369 Die Struktur von Magnesiumchlorid- und Magnesiumbromidhexahydrat. _cod_database_code 1011249 _database_code_amcsd 0018111 CELL PARAMETERS: 9.9000 7.1500 6.1000 90.000 94.000 90.000 SPACE GROUP: C2/m X-RAY WAVELENGTH: 1.541838 Cell Volume: 430.737 Density (g/cm3): 1.474 MAX. ABS. INTENSITY / VOLUME**2: 5.507378909 RIR: 1.217 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.56 1.12 6.0851 0 0 1 2 15.30 21.71 5.7915 1 1 0 4 17.96 1.05 4.9379 2 0 0 2 20.74 14.25 4.2836 -1 1 1 4 21.61 100.00 4.1120 1 1 1 4 22.38 25.37 3.9723 -2 0 1 2 23.99 5.28 3.7098 2 0 1 2 24.91 26.07 3.5750 0 2 0 2 29.35 1.62 3.0426 0 0 2 2 29.88 35.85 2.9902 3 1 0 4 30.88 45.45 2.8958 2 2 0 4 32.52 13.68 2.7537 -3 1 1 4 32.68 39.92 2.7400 -1 1 2 4 33.50 13.64 2.6750 -2 0 2 2 33.73 41.80 2.6573 -2 2 1 4 33.84 28.99 2.6492 1 1 2 4 34.24 3.31 2.6188 3 1 1 4 34.85 5.60 2.5742 2 2 1 4 36.39 5.60 2.4690 4 0 0 2 38.38 6.71 2.3455 -4 0 1 2 38.87 19.74 2.3170 0 2 2 4 38.87 4.57 2.3168 1 3 0 4 40.37 28.85 2.2342 4 0 1 2 40.96 1.40 2.2036 -3 1 2 4 41.48 2.78 2.1771 -1 3 1 4 41.95 6.14 2.1535 1 3 1 4 42.19 1.97 2.1418 -2 2 2 4 43.77 5.50 2.0682 3 1 2 4 44.04 11.27 2.0560 2 2 2 4 47.07 1.23 1.9305 3 3 0 4 47.24 3.40 1.9240 -2 0 3 2 48.02 4.12 1.8946 4 2 1 4 49.03 29.55 1.8580 -1 3 2 4 49.17 11.08 1.8529 -5 1 1 4 49.77 4.68 1.8319 2 0 3 2 50.16 6.69 1.8188 3 3 1 4 51.10 9.77 1.7875 0 4 0 2 51.23 7.14 1.7832 5 1 1 4 51.82 4.78 1.7642 0 2 3 4 52.72 9.12 1.7362 -4 2 2 4 52.91 5.51 1.7303 -3 1 3 4 54.13 3.71 1.6942 -2 2 3 4 55.86 3.22 1.6460 6 0 0 2 56.40 2.16 1.6313 3 1 3 4 56.45 4.38 1.6301 -2 4 1 4 57.58 4.88 1.6007 3 3 2 4 58.93 2.14 1.5672 5 1 2 4 61.22 2.08 1.5139 1 3 3 4 62.08 3.79 1.4951 6 2 0 4 62.11 11.33 1.4944 -5 3 1 4 62.48 3.50 1.4864 -1 1 4 4 62.63 4.39 1.4833 -2 0 4 2 62.86 3.14 1.4785 -4 2 3 4 63.08 2.53 1.4737 -6 2 1 4 65.19 3.46 1.4311 6 2 1 4 65.35 1.61 1.4279 -3 3 3 4 65.44 2.82 1.4261 2 0 4 2 66.01 1.32 1.4152 1 5 0 4 66.83 3.51 1.3998 0 2 4 4 67.05 6.87 1.3959 4 2 3 4 67.05 4.82 1.3958 4 4 1 4 68.18 3.39 1.3754 1 5 1 4 68.45 4.14 1.3707 3 3 3 4 70.01 1.26 1.3438 5 1 3 4 70.39 1.08 1.3375 -4 0 4 2 70.73 1.09 1.3320 5 3 2 4 71.18 1.81 1.3246 2 2 4 4 71.21 3.34 1.3241 -6 0 3 2 72.00 3.30 1.3116 3 5 0 4 72.13 1.28 1.3096 -2 4 3 4 73.15 2.84 1.2937 -7 1 2 4 73.43 1.05 1.2896 -3 5 1 4 74.18 2.70 1.2783 1 5 2 4 76.76 1.16 1.2417 -6 2 3 4 78.61 1.02 1.2170 0 0 5 2 79.09 1.74 1.2108 6 4 0 4 80.62 1.74 1.1917 0 6 0 2 83.28 1.80 1.1602 -8 2 1 4 83.63 1.07 1.1563 4 4 3 4 83.92 1.69 1.1530 -3 1 5 4 84.04 2.06 1.1517 -7 3 2 4 84.97 1.48 1.1415 -2 4 4 4 84.97 1.15 1.1414 -2 6 1 4 86.09 1.94 1.1294 5 5 1 4 87.42 1.23 1.1156 -3 5 3 4 87.50 1.57 1.1148 2 4 4 4 88.67 2.20 1.1031 3 1 5 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.