Sassolite Zachariasen W H Zeitschrift fur Kristallographie 88 (1934) 150-161 The crystal lattice of boric acid, BO3H3 Locality: synthetic _database_code_amcsd 0018735 CELL PARAMETERS: 7.0500 7.0500 6.5700 92.500 101.170 120.000 SPACE GROUP: P-1 X-RAY WAVELENGTH: 1.541838 Cell Volume: 273.621 Density (g/cm3): 1.501 MAX. ABS. INTENSITY / VOLUME**2: 7.393742174 RIR: 1.604 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.57 17.85 6.0811 -1 1 0 2 14.71 19.57 6.0214 0 1 0 2 14.98 28.46 5.9130 1 0 0 2 18.55 5.44 4.7843 0 -1 1 2 19.28 6.01 4.6042 -1 1 1 2 21.10 4.70 4.2106 1 -1 1 2 21.95 3.44 4.0500 0 1 1 2 28.07 100.00 3.1784 0 0 2 2 28.38 4.87 3.1454 -1 0 2 2 29.53 2.81 3.0249 0 -1 2 2 29.67 1.30 3.0107 0 2 0 2 30.23 10.09 2.9565 2 0 0 2 30.55 2.24 2.9261 -1 1 2 2 30.68 8.54 2.9137 0 -2 1 2 31.46 8.61 2.8435 -2 2 1 2 32.94 1.74 2.7190 1 -1 2 2 33.79 6.76 2.6524 2 -2 1 2 34.00 1.75 2.6366 0 1 2 2 35.02 5.45 2.5620 0 2 1 2 35.23 2.35 2.5474 1 0 2 2 35.97 5.59 2.4971 -2 0 2 2 39.40 2.69 2.2870 -3 1 1 2 39.42 3.90 2.2857 -1 -2 1 2 39.82 4.55 2.2637 -3 2 1 2 40.08 1.89 2.2498 -3 1 0 2 40.36 3.52 2.2346 2 1 0 2 40.49 3.84 2.2278 1 -3 1 2 41.58 3.16 2.1722 -2 3 1 2 41.70 3.12 2.1661 2 -3 1 2 43.08 3.03 2.0997 -1 3 1 2 43.29 2.69 2.0899 -2 -1 2 2 43.82 1.34 2.0659 -3 1 2 2 44.39 2.99 2.0407 3 -2 1 2 45.58 2.22 1.9901 1 2 1 2 45.67 1.52 1.9864 3 -1 1 2 46.90 2.03 1.9374 2 0 2 2 48.26 1.61 1.8858 0 -2 3 2 50.24 1.49 1.8161 -2 2 3 2 52.43 1.23 1.7452 -1 -2 3 2 54.11 1.29 1.6948 -3 2 3 2 54.25 1.07 1.6907 -1 -3 1 2 54.99 1.02 1.6700 2 -2 3 2 58.04 6.12 1.5892 0 0 4 2 82.19 1.39 1.1729 -3 -3 1 2 86.75 1.15 1.1226 -3 -3 3 2 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.