Cr Cs2 O4 Miller J Zeitschrift fur Kristallographie 99 (1938) 32-37 The Crystal Structure of Caesium Chromate Cs2 Cr O4 _cod_database_code 1010443 _database_code_amcsd 0017364 CELL PARAMETERS: 6.2260 11.1350 8.3630 90.000 90.000 90.000 SPACE GROUP: Pmcn X-RAY WAVELENGTH: 1.541838 Cell Volume: 579.778 Density (g/cm3): 4.373 MAX. ABS. INTENSITY / VOLUME**2: 54.56321035 RIR: 4.062 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.24 1.70 6.6870 0 1 1 4 16.31 2.10 5.4342 1 1 0 4 19.48 6.31 4.5567 1 1 1 8 21.25 1.35 4.1815 0 0 2 2 22.72 9.98 3.9146 0 1 2 4 23.94 50.82 3.7176 1 2 1 8 25.66 5.78 3.4713 1 0 2 4 26.27 14.15 3.3925 0 3 1 4 26.66 42.55 3.3435 0 2 2 4 26.90 100.00 3.3140 1 1 2 8 27.99 96.62 3.1881 1 3 0 4 28.68 64.67 3.1130 2 0 0 2 30.34 11.07 2.9456 1 2 2 8 32.15 3.20 2.7838 0 4 0 2 32.25 8.17 2.7759 0 3 2 4 33.13 32.21 2.7042 0 1 3 4 33.94 7.19 2.6413 0 4 1 4 34.71 7.96 2.5841 2 2 1 8 35.41 2.54 2.5353 1 3 2 8 36.22 1.02 2.4803 1 1 3 8 36.89 14.06 2.4365 2 1 2 8 36.97 10.71 2.4315 1 4 1 8 38.86 6.91 2.3172 0 4 2 4 38.92 2.35 2.3141 1 2 3 8 39.28 14.93 2.2937 2 3 1 8 39.55 31.92 2.2784 2 2 2 8 40.47 6.65 2.2290 0 3 3 4 41.59 3.22 2.1717 1 4 2 8 41.98 11.92 2.1520 0 5 1 4 43.11 1.03 2.0986 1 3 3 8 43.14 2.38 2.0969 1 5 0 4 43.27 2.99 2.0907 0 0 4 2 43.69 8.53 2.0718 2 3 2 8 44.37 17.50 2.0415 2 1 3 8 45.01 2.67 2.0140 2 4 1 8 45.78 1.70 1.9821 3 1 1 8 45.78 6.08 1.9820 1 0 4 4 46.18 2.57 1.9656 0 5 2 4 46.39 2.14 1.9573 0 2 4 4 46.54 6.03 1.9513 1 1 4 8 48.03 5.81 1.8941 3 2 1 8 48.47 25.44 1.8780 1 4 3 8 48.57 1.29 1.8744 1 5 2 8 49.00 1.68 1.8590 3 0 2 4 49.01 3.69 1.8588 2 4 2 8 49.09 2.52 1.8558 0 6 0 2 49.73 13.94 1.8336 3 1 2 8 50.07 4.62 1.8216 0 3 4 4 50.35 2.03 1.8123 2 3 3 8 50.38 15.37 1.8114 3 3 0 4 51.63 12.38 1.7702 2 5 1 8 51.85 1.82 1.7633 3 2 2 8 52.33 3.36 1.7483 1 3 4 8 52.61 5.43 1.7396 1 6 1 8 52.74 3.83 1.7356 2 0 4 4 54.06 4.29 1.6963 0 6 2 4 55.45 2.62 1.6570 2 2 4 8 55.56 1.49 1.6540 0 1 5 4 56.20 4.40 1.6366 1 6 2 8 56.38 2.21 1.6319 3 4 1 8 57.54 3.73 1.6019 0 2 5 4 57.66 2.58 1.5986 1 1 5 8 57.84 4.85 1.5941 2 6 0 4 58.73 6.77 1.5722 2 3 4 8 59.38 8.46 1.5565 4 0 0 2 59.59 7.26 1.5513 1 2 5 8 59.82 1.52 1.5460 3 4 2 8 60.03 4.18 1.5412 1 7 0 4 60.76 1.03 1.5243 0 5 4 4 61.03 1.33 1.5183 3 5 0 4 61.88 3.92 1.4993 1 6 3 8 62.34 7.19 1.4895 2 6 2 8 63.12 3.04 1.4729 3 0 4 4 63.71 1.03 1.4607 2 1 5 8 63.74 1.95 1.4602 3 1 4 8 64.42 1.19 1.4464 4 1 2 8 65.31 10.67 1.4287 3 4 3 8 65.54 6.67 1.4244 2 2 5 8 66.04 1.94 1.4147 4 3 1 8 66.23 5.23 1.4111 4 2 2 8 67.16 1.61 1.3938 0 0 6 2 67.27 1.91 1.3919 0 8 0 2 67.83 3.58 1.3816 0 7 3 4 68.52 1.97 1.3694 2 3 5 8 68.54 1.34 1.3690 3 3 4 8 68.78 2.46 1.3648 3 6 1 8 69.20 1.39 1.3576 4 3 2 8 69.37 1.15 1.3547 1 6 4 8 69.71 4.89 1.3490 4 1 3 8 70.18 1.11 1.3410 4 4 1 8 70.20 2.09 1.3408 1 8 1 8 70.40 3.36 1.3374 0 5 5 4 71.39 1.14 1.3213 1 2 6 8 71.89 1.45 1.3134 3 6 2 8 72.25 5.30 1.3076 1 5 5 8 73.17 1.33 1.2935 3 1 5 8 73.26 1.45 1.2921 4 4 2 8 74.26 1.53 1.2771 1 3 6 8 74.33 1.36 1.2762 4 3 3 8 74.60 1.40 1.2721 2 0 6 4 74.70 3.05 1.2706 2 8 0 4 74.88 2.73 1.2681 3 2 5 8 75.17 1.54 1.2639 2 1 6 8 75.25 7.40 1.2628 2 7 3 8 75.27 2.05 1.2625 3 7 0 4 75.36 3.55 1.2612 4 5 1 8 76.94 1.51 1.2392 3 6 3 8 77.71 4.87 1.2288 2 5 5 8 79.74 1.56 1.2025 5 2 1 8 80.55 1.06 1.1926 4 6 0 4 81.03 3.49 1.1866 5 1 2 8 81.05 1.06 1.1864 0 9 2 4 81.31 2.03 1.1834 4 3 4 8 81.54 3.35 1.1805 5 3 0 4 82.70 2.57 1.1668 1 1 7 8 82.83 5.30 1.1654 1 9 2 8 84.48 2.17 1.1468 4 6 2 8 84.64 1.37 1.1451 3 8 1 8 86.59 3.03 1.1242 3 5 5 8 87.35 2.06 1.1163 4 2 5 8 88.12 1.13 1.1086 2 9 2 8 89.21 2.67 1.0979 0 4 7 4 89.64 1.05 1.0937 2 2 7 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.