Pollucite Naray-Szabo S Zeitschrift fur Kristallographie 99 (1938) 277-282 Die Struktur des Pollucits (Cs Al Si2 O6)*(H2 O)X _cod_database_code 1011122 _database_code_amcsd 0018016 CELL PARAMETERS: 13.7400 13.7400 13.7400 90.000 90.000 90.000 SPACE GROUP: Ia3d X-RAY WAVELENGTH: 1.541838 Cell Volume: 2593.941 Density (g/cm3): 3.196 MAX. ABS. INTENSITY / VOLUME**2: 60.83920769 RIR: 6.199 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 15.80 8.32 5.6093 2 1 1 24 24.24 53.23 3.6722 3 2 1 48 25.94 100.00 3.4350 4 0 0 6 30.52 47.26 2.9294 3 3 2 24 33.25 2.38 2.6946 4 3 1 48 35.79 9.40 2.5086 5 2 1 48 37.01 33.26 2.4289 4 4 0 12 40.47 1.59 2.2289 6 1 1 24 40.47 17.23 2.2289 5 3 2 48 44.73 8.98 2.0259 6 3 1 48 45.75 4.40 1.9832 4 4 4 8 47.73 1.03 1.9054 6 4 0 24 48.70 9.92 1.8698 7 2 1 48 48.70 8.95 1.8698 6 3 3 24 48.70 4.05 1.8698 5 5 2 24 52.44 21.13 1.7450 7 3 2 48 52.44 2.83 1.7450 6 5 1 48 53.34 8.22 1.7175 8 0 0 6 54.24 1.19 1.6913 7 4 1 48 55.99 4.61 1.6422 6 5 3 48 59.41 6.69 1.5557 7 5 2 48 60.24 11.68 1.5362 8 4 0 24 62.71 3.79 1.4816 7 6 1 48 62.71 1.57 1.4816 6 5 5 24 65.91 7.10 1.4172 7 6 3 48 66.70 4.26 1.4023 8 4 4 24 69.04 5.24 1.3605 7 7 2 24 69.04 3.22 1.3605 10 1 1 24 72.10 2.71 1.3101 7 6 5 48 72.10 5.61 1.3101 10 3 1 48 72.10 1.96 1.3101 9 5 2 48 73.61 1.02 1.2869 8 7 1 48 75.10 2.90 1.2649 10 3 3 24 78.07 4.90 1.2241 10 5 1 48 78.81 2.24 1.2145 8 8 0 12 81.01 3.58 1.1870 10 5 3 48 81.01 2.00 1.1870 11 3 2 48 81.01 2.05 1.1870 7 7 6 24 83.92 1.01 1.1530 9 6 5 48 84.64 1.01 1.1450 12 0 0 6 84.64 2.50 1.1450 8 8 4 24 86.81 2.52 1.1219 10 5 5 24 86.81 2.05 1.1219 11 5 2 48 86.81 2.22 1.1219 10 7 1 48 89.70 2.46 1.0931 10 7 3 48 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.