Li10 Pb3 Rollier M, Arreghini E Zeitschrift fur Kristallographie 101 (1939) 470-482 La fase gamma della lega litio-piombo Li10 Pb3 _cod_database_code 1010455 _database_code_amcsd 0017375 CELL PARAMETERS: 10.0820 10.0820 10.0820 90.000 90.000 90.000 SPACE GROUP: P-43m X-RAY WAVELENGTH: 1.541838 Cell Volume: 1024.802 Density (g/cm3): 4.478 MAX. ABS. INTENSITY / VOLUME**2: 178.8418135 RIR: 13.004 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 8.77 4.82 10.0820 1 0 0 6 12.42 34.55 7.1291 1 1 0 12 15.22 21.92 5.8208 1 1 1 4 17.59 6.24 5.0410 2 0 0 6 19.69 42.12 4.5088 2 1 0 24 21.59 25.15 4.1160 2 1 1 12 24.98 12.31 3.5645 2 2 0 12 26.52 40.53 3.3607 2 2 1 12 26.52 59.47 3.3607 3 0 0 6 27.99 2.04 3.1882 3 1 0 24 29.38 12.32 3.0398 3 1 1 12 30.72 19.46 2.9104 2 2 2 4 32.01 3.04 2.7962 3 2 0 24 33.25 31.95 2.6945 3 2 1 24 35.62 1.60 2.5205 4 0 0 6 36.75 13.09 2.4452 3 2 2 12 37.86 18.56 2.3764 4 1 1 12 37.86 41.82 2.3764 3 3 0 12 38.94 3.07 2.3130 3 3 1 12 39.99 2.39 2.2544 4 2 0 24 41.02 1.92 2.2001 4 2 1 24 42.03 2.81 2.1495 3 3 2 12 44.96 2.67 2.0164 4 3 0 24 44.96 3.96 2.0164 5 0 0 6 45.90 4.23 1.9772 5 1 0 24 45.90 1.44 1.9772 4 3 1 24 46.82 6.44 1.9403 5 1 1 12 46.82 9.05 1.9403 3 3 3 4 48.63 1.38 1.8722 5 2 0 24 48.63 3.82 1.8722 4 3 2 24 49.52 18.90 1.8407 5 2 1 24 52.11 11.60 1.7551 5 2 2 12 52.11 13.44 1.7551 4 4 1 12 52.96 6.62 1.7290 5 3 0 24 52.96 2.06 1.7290 4 3 3 12 53.79 6.54 1.7042 5 3 1 24 54.62 2.15 1.6803 4 4 2 12 54.62 3.17 1.6803 6 0 0 6 56.25 3.77 1.6355 5 3 2 24 56.25 2.18 1.6355 6 1 1 12 58.63 1.07 1.5745 5 4 0 24 58.63 7.02 1.5745 6 2 1 24 59.41 1.66 1.5557 5 4 1 24 60.19 3.03 1.5375 5 3 3 12 60.96 4.26 1.5199 6 2 2 12 61.72 2.70 1.5029 5 4 2 24 61.72 5.03 1.5029 6 3 0 24 62.48 3.68 1.4865 6 3 1 24 63.98 5.02 1.4552 4 4 4 4 64.72 2.28 1.4403 6 3 2 24 65.46 2.40 1.4258 5 4 3 24 66.20 3.36 1.4118 7 1 1 12 66.20 3.43 1.4118 5 5 1 12 68.37 1.89 1.3720 7 2 1 24 68.37 4.25 1.3720 5 5 2 12 68.37 3.82 1.3720 6 3 3 12 69.81 1.76 1.3473 6 4 2 24 73.34 1.56 1.2909 6 4 3 24 74.04 3.53 1.2804 6 5 1 24 75.43 1.74 1.2602 8 0 0 6 76.12 2.84 1.2505 6 5 2 24 76.81 9.11 1.2410 7 4 1 24 76.81 1.53 1.2410 8 1 1 12 78.86 3.03 1.2137 8 2 1 24 78.86 1.55 1.2137 7 4 2 24 79.55 1.19 1.2050 6 5 3 24 80.91 1.72 1.1882 8 2 2 12 81.58 1.57 1.1800 6 6 1 12 81.58 3.73 1.1800 8 3 0 24 83.61 1.64 1.1565 6 6 2 12 84.28 1.49 1.1490 6 5 4 24 86.97 1.00 1.1202 6 6 3 12 86.97 5.01 1.1202 7 4 4 12 86.97 1.52 1.1202 8 4 1 24 87.64 2.35 1.1134 8 3 3 12 88.98 1.10 1.1000 8 4 2 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.