Bi0.67 O1.33 Pb0.33 Sillen L, Aurivillius B Zeitschrift fur Kristallographie 101 (1939) 483-495 Oxide phases with a defect oxygen lattice _cod_database_code 1010020 _database_code_amcsd 0016959 CELL PARAMETERS: 4.0500 4.0500 4.9000 90.000 90.000 90.000 SPACE GROUP: P4/nmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 80.372 Density (g/cm3): 9.496 MAX. ABS. INTENSITY / VOLUME**2: 642.1265110 RIR: 22.019 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.10 4.15 4.9000 0 0 1 2 28.59 100.00 3.1217 1 0 1 8 31.23 45.32 2.8638 1 1 0 4 36.68 11.64 2.4500 0 0 2 2 43.15 6.09 2.0963 1 0 2 8 44.75 19.17 2.0250 2 0 0 4 48.65 1.07 1.8715 2 0 1 8 48.93 23.71 1.8617 1 1 2 8 53.97 30.45 1.6989 2 1 1 16 59.20 10.18 1.5609 2 0 2 8 61.19 8.01 1.5148 1 0 3 8 63.92 3.15 1.4564 2 1 2 16 65.15 5.23 1.4319 2 2 0 4 65.83 2.46 1.4188 1 1 3 8 72.64 5.45 1.3015 3 0 1 8 74.02 5.68 1.2807 3 1 0 8 74.66 1.15 1.2713 2 0 3 8 77.16 4.07 1.2362 2 2 2 8 78.92 6.61 1.2130 2 1 3 16 82.22 2.05 1.1725 1 0 4 8 85.57 6.91 1.1350 3 1 2 16 86.39 1.55 1.1263 1 1 4 8 89.52 5.70 1.0949 3 2 1 16 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.