Goethite Hoppe W Zeitschrift fur Kristallographie 103 (1940) 73-89 Uber die kristallstruktur von alpha-AlOOH (diaspore) und alpha-Fe OOH(nadeleisenerz) Locality: Synthetic _database_code_amcsd 0010571 CELL PARAMETERS: 4.5900 10.0000 3.0300 90.000 90.000 90.000 SPACE GROUP: Pbnm X-RAY WAVELENGTH: 1.541838 Cell Volume: 139.077 Density (g/cm3): 4.195 MAX. ABS. INTENSITY / VOLUME**2: 38.75306407 RIR: 3.008 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.74 12.39 5.0000 0 2 0 2 21.30 100.00 4.1716 1 1 0 4 26.36 10.64 3.3813 1 2 0 4 33.22 41.85 2.6971 1 3 0 4 34.62 27.55 2.5913 0 2 1 4 35.50 4.99 2.5287 1 0 1 4 35.92 13.45 2.5000 0 4 0 2 36.66 77.80 2.4515 1 1 1 8 39.26 4.18 2.2950 2 0 0 2 39.95 10.02 2.2565 1 2 1 8 40.32 1.76 2.2368 2 1 0 4 41.11 14.63 2.1955 1 4 0 4 43.38 1.94 2.0858 2 2 0 4 45.00 3.60 2.0146 1 3 1 8 47.13 6.25 1.9284 0 4 1 4 50.73 10.51 1.7996 2 1 1 8 51.40 1.87 1.7778 1 4 1 8 53.32 34.99 1.7181 2 2 1 8 54.26 11.46 1.6906 2 4 0 4 55.10 4.02 1.6667 0 6 0 2 57.46 7.37 1.6038 2 3 1 8 58.87 24.44 1.5687 1 5 1 8 61.18 10.73 1.5150 0 0 2 2 61.50 4.39 1.5078 2 5 0 4 62.96 3.12 1.4764 2 4 1 8 63.60 4.84 1.4630 3 2 0 4 63.73 11.23 1.4603 0 6 1 4 65.55 6.14 1.4240 1 1 2 8 67.34 5.57 1.3905 3 3 0 4 67.78 1.04 1.3826 1 2 2 8 68.73 3.39 1.3658 3 0 1 4 68.83 6.39 1.3640 1 7 0 4 69.46 1.95 1.3532 3 1 1 8 69.73 2.17 1.3486 2 6 0 4 71.41 7.10 1.3209 1 3 2 8 71.63 1.59 1.3175 3 2 1 8 73.03 2.76 1.2957 0 4 2 4 75.14 1.33 1.2644 2 0 2 4 75.18 2.34 1.2638 3 3 1 8 76.38 2.33 1.2469 1 4 2 8 80.06 3.47 1.1986 3 4 1 8 83.70 2.44 1.1555 0 8 1 4 85.10 2.99 1.1400 4 1 0 4 86.20 4.33 1.1283 2 4 2 8 86.24 1.53 1.1279 3 5 1 8 86.89 1.63 1.1211 0 6 2 4 89.22 1.17 1.0977 2 8 0 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.