Co3B2O6 Newnham R E, Redman M J, Santoro R P Zeitschrift fur Kristallographie 121 (1965) 418-424 Neutron-diffraction study of Co3B2O6 _database_code_amcsd 0010624 CELL PARAMETERS: 5.4620 8.4360 4.5290 90.000 90.000 90.000 SPACE GROUP: Pnmn X-RAY WAVELENGTH: 1.541838 Cell Volume: 208.685 Density (g/cm3): 4.685 MAX. ABS. INTENSITY / VOLUME**2: 36.39422361 RIR: 2.530 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 21.06 3.09 4.2180 0 2 0 2 22.28 50.98 3.9903 0 1 1 4 25.55 22.08 3.4864 1 0 1 4 27.69 2.36 3.2221 1 1 1 8 32.79 9.55 2.7310 2 0 0 2 33.34 100.00 2.6873 1 2 1 8 35.92 50.59 2.5001 1 3 0 4 37.65 6.18 2.3890 0 3 1 4 38.49 3.73 2.3387 2 0 1 4 39.30 2.79 2.2924 2 2 0 4 39.81 9.36 2.2645 0 0 2 2 40.01 58.34 2.2537 2 1 1 8 41.25 14.58 2.1888 1 3 1 8 43.25 1.80 2.0918 1 0 2 4 50.58 11.55 1.8045 1 4 1 8 50.78 4.43 1.7981 2 3 1 8 52.49 34.39 1.7432 2 0 2 4 54.30 1.59 1.6893 3 0 1 4 54.69 42.64 1.6784 1 3 2 8 55.01 1.33 1.6692 2 4 0 4 57.14 1.15 1.6120 1 5 0 4 58.37 9.41 1.5811 0 5 1 4 58.89 15.08 1.5682 3 2 1 8 59.94 1.44 1.5433 0 4 2 4 60.59 19.89 1.5283 3 3 0 4 62.50 6.25 1.4861 0 1 3 4 66.50 7.36 1.4060 0 6 0 2 68.17 8.87 1.3756 1 2 3 8 68.58 13.33 1.3683 2 5 1 8 68.74 6.23 1.3655 4 0 0 2 70.84 1.80 1.3301 0 3 3 4 71.56 2.53 1.3185 3 4 1 8 72.40 3.61 1.3053 2 1 3 8 73.24 1.45 1.2923 1 3 3 8 73.27 3.37 1.2919 4 1 1 8 74.97 6.57 1.2668 3 3 2 8 76.15 2.28 1.2501 2 6 0 4 80.13 1.73 1.1977 1 4 3 8 80.39 2.62 1.1945 0 6 2 4 81.13 1.08 1.1855 4 3 1 8 82.49 3.62 1.1694 4 0 2 4 85.82 2.87 1.1322 0 0 4 2 86.51 2.25 1.1250 0 5 3 4 86.96 4.52 1.1204 3 2 3 8 89.57 7.36 1.0944 2 6 2 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.